Effect of Electrolyte Composition on Ni-Fe Deposition in LIGA Process
電鍍液成份對LIGA程序中電鑄鎳鐵合金的效應探討
摘要
本文在闡述微系統工程（ＭＥＭＳ），鎳鐵合金鍍液的表面張力對電鑄微結構性質的影響。在高深寬比（深210μm，寬度僅有7μm）的微孔內進行電鑄程序，可以製造出鎳鐵合金的微結構。結構的內應力與表面完整性會受到鍍液內界面活性劑以及電流密度所影響。藉由界面活性劑的添加輔以控制適當的電流密度，即可藉由電鍍本身所伴隨的析氫反應，來促進微孔內的流動性質，用以減少微孔內由於電化學反應所造成的pH值變化。
關鍵字
無資料並列摘要
The effect of electrolyte's surface tension on Ni-Fe codeposition for MEMS application was studied. A nickel-iron microstructure was obtained inside high-aspect-ratio(210μm deep with 7μm width) microchannel. The internal stress and surface defect of the alloy microstructure are influenced by the presence of surfactant and applied current. Uniform distribution of deposit inside microstructure can be achieved by choosing proper current, surfactant and optimal control of hydrogen evolution reaction which can induce agitation and mitigate pH variation during electrodeposition.
延伸閱讀
- 黃彥鈞（2014）。無電解電鍍鎳液的安定劑成份分析及功能性試驗〔碩士論文，朝陽科技大學〕。華藝線上圖書館。https://www.airitilibrary.com/Article/Detail?DocID=U0078-2502201617123778
- 林柏廷（1994）。以電壓動態及穩態實驗方法研究鎳鐵合金電鍍過程〔碩士論文，元智大學〕。華藝線上圖書館。https://www.airitilibrary.com/Article/Detail?DocID=U0009-0112200611313965
- 許杰（1993）。以數學模式模擬鎳鐵合金電鍍過程中加入表面活性劑之行為〔碩士論文，元智大學〕。華藝線上圖書館。https://www.airitilibrary.com/Article/Detail?DocID=U0009-0112200611343793
- Hsu, C. H., Lee, H. B., Lin, C. S., & Lee, C. Y. (2011). 電鍍鎳磷合金微構形結構之電催化活性研究. 中國機械工程學刊, 32(2), 103-109. https://doi.org/10.29979/JCSME.201104.0002
- 陳弘毅（2011）。電漿熔射噴塗製備鎳銅合金/氧化鈰複合陽極之製程研究與性質探討〔碩士論文，國立臺北科技大學〕。華藝線上圖書館。https://doi.org/10.6841/NTUT.2011.00448