ABS/PC/MMT複合材料之製備與性質研究

本研究以ABS/PC作為基材，其含量為70/30與30/70 wt%，之後再分別添加不同含量1.5、3、4.5及6%之MMT於ABS/PC (70/30與30/70 wt%)中，經捏合機混煉後利用射出成形製作出複合材料，探討在添加不同含量MMT複合材料之熱性質、機械性質。經由捏合機混練，再由射出成形機製備出ABS/PC/MMT之複合材料試片，利用熱示差掃描分析儀、熱重分析儀與熱傳導分析儀測試其熱性質。以及使用萬能試驗機、衝擊試驗機與磨耗試驗機來測試其機械性質。熱性質由實驗結果得知，添加MMT到ABS/PC複合材料中，在玻璃轉移溫度、裂解溫度和熱傳導係數有上升的趨勢，結果顯示添加MMT可獲得良好的改良效果。機械性質由實驗結果得知，拉伸強度和衝擊強度隨著MMT含量增加而下降；磨耗損失隨著MMT含量的增加而下降，耐磨耗則有大幅提升。

關鍵字

MMT ；複合材料；熱性質；機械性質

並列摘要

The purpose of this research is to prepare ABS/PC (70/30 and 30/70 wt%) composites with MMT by different content from 1.5、3、4.5 to 6%. The kneader was used to prepare the composites. The thermal properties, mechanical properties of the composites were measured. We use kneader to melt the composites, and use injection molding to obtain the specimen. The thermal properties, of the ABS/PC/MMT composites were studied by Thermogravimetry(TGA), differential scanning calorimetry(DSC), and Thermal Conductivity Analyzer. The mechanical properties of ABS/PC/MMT composite were studied by Universal Testing Machine, Izod Impact Tester and Wear Instruments,respectively. The EMI SE properties of ABS/PC/MMT composite were studied by Spectrum Analyzer. The experimental results, show that the glass transition temperature, decomposition temperature, and thermal conductivity increase with the content of the MMT.The mechanical properties, however, the tensile strenhth, impact strength, and wear decrease with the MMT content.