硝酸鈉對碳鋼抗蝕性之影響

The Effect of Sodium Nitrate on the Corrosion Resistance of Carbon Steel

方又興(Y. S. Fang) ； 徐聰仁(C. J. Hsu)

《防蝕工程》 7卷3期 (1993/09) Pp. 1-9

https://doi.org/10.6376/JCCE.199309.0001

摘要

本研究以動電位極化掃描方法探討：(1)硝酸鈉在氯化鈉水溶液中對碳鋼抗蝕性之影響；(2)鉻酸鹽在pH=3之硝酸鈉水溶液中的抑制行為。其結果歸納如下：1．當pH=3時，腐蝕速率隨硝酸根離子濃度增加而上昇。在pH=5和11時，腐蝕速率隨硝酸根離子濃度增加而下降。在pH=7和9時若硝酸鈉濃度大於0.2M，腐蝕速率異常昇高。2．鉻酸鹽在pH=3的硝酸鈉溶液中為腐蝕抑制劑。

並列摘要

The study was executed by potentiodynamic polarization method to investigate: (1)the effect of sodium nitrate on the corrosion of carbon steel in sodium chloride aqueous solutions; (2)the inhibition effect of chromate on the corrsion of-carbon steel in sodium nitrate aqueous solutionat pH=3. The results are summarlzed as follows: 1. At pH=3,the corrosion rate increases with the increasing concentration of NO3(superscript -).At pH=5 and 11,the corrosion rate decreases with the increasing concentration of NO3(superscript -). At pH=7 and 9, if [NaNO3]≥0.2M the corrosion rate increases unnaturally. 2.Chromate acts as an inhibitor in sodium nitrate solutions.

並列關鍵字

Inhibition effects of sodium nitrate ； Effect on carbon steel corrosion ； by pH and chromate