表面塗對A516壓力容器用鋼及304不銹鋼在400℃模擬海水環境下之抗腐蝕性質研究
Effect of Surface Coating on the Corrosion Behavior of A516 Pressurized-Vessel Steel and 304 Stainless Steel at 400℃ in a Simulated NaCl-Containing Atmosphere
摘要
本研究主要探討表面塗裝改質對A516壓力容器用鋼及304不銹鋼在400℃模擬海水環境之抗蝕性能。研究結果顯示，在模擬含NaCl之水汽環境下，兩式鋼材經表面塗裝之腐蝕動力學皆遵守拋物線定律，而A516鋼材之腐蝕速率較304不銹鋼略快。兩式鋼材經表面塗裝改質後之腐蝕生成物皆含有氧化矽(SiO2)及氧化鈦(TiO2)，並含有微量的氧化鈦鐵(Fe2TiO5)。
並列摘要
The effect of surface coating on the corrosion behavior of A516 pressurized-vessel steel (A516) and 304 stainless steel (304SS) at 400℃ in a simulated NaCl-containing environment was investigated. The results showed that the corrosion kinetics at 400℃ for both steels obeyed the parabolic rate law. The corrosion rate of A516 was slightly faster than that of 304SS.The scales formed on both A516 and 304SS consisted of SiO2, TiO2, and minor Fe2TiO5.
延伸閱讀
- 林東和、游輝哲、開物、開執中（1997）。A516壓力容器用鋼在含NaCl水汽環境的腐蝕行為。防蝕工程，11(3)，131-139。https://doi.org/10.6376/JCCE.199709.0131
- 王佰揚、葉宗洸、蔡春鴻（2006）。不同抑制性被覆條件之304不銹鋼在高溫純水環境中的電化學行為研究。防蝕工程，20(3)，209-232。https://doi.org/10.6376/JCCE.200609.0209
- 邱又文（2014）。304不銹鋼於模擬沸水式反應器起動狀態之水化學環境中的應力腐蝕龜裂行為研究〔碩士論文，國立清華大學〕。華藝線上圖書館。https://www.airitilibrary.com/Article/Detail?DocID=U0016-3103201511190741
- 黃冠儒、葉宗洸、蔡春鴻（2009）。高溫純水中82合金與304低碳不銹鋼異材銲件之應力腐蝕研究。防蝕工程，23(3)，213-226。https://doi.org/10.6376/JCCE.200909.0213
- 徐一仁、李綺芳、林宗岳、李雅榮、李岳聯（2020）。Declining Model of Mechanical Properties for Corroded Steel Plate: An Empirical Study of Real Ships and Accelerated Corrosion Test。防蝕工程，34(4)，22-32。https://doi.org/10.6376/JCCE.202012_34(4).0003