腐蝕抑制劑對Fe-Co-Ni-Cu-Al高熵合金在3.5%NaCl水溶液中之抑制效應

Effects of Corrosion Inhibitors on the Fe-Co-Ni-Cu-Al High Entropy Alloy in 3.5% NaCl Solution

葉威德(W. D. Yeh) ； 陳柏洲(P. C. Chen) ； 開物(W. Kai) ； 吳建國(J. K. Wu)

《防蝕工程》 18卷3期 (2004/09) Pp. 273-280

https://doi.org/10.6376/JCCE.200409.0273

摘要

本研究主要探討三種腐蝕抑制劑對FeCoNiCuAl高熵合金3.5%NaCl水溶液中的抑制行為。由電化學實驗結果得知，三種抑制劑中，添加Na3PO4將使高鏑合金的孔蝕電位值（E(下標 pit)）最高且鈍化區（△E(下標 p)）範圍最大，NaNO2次之，而Na2MoO4最小；同時，鈍化電流密度（I (下標 pass)）則以Na3PO4最小，Na2MoO4次之，NaNO2最大，顯示添加Na3PO4對高熵合金的腐蝕抑制效果最好。

關鍵字

腐蝕抑制劑 ； 高熵合金(FeCoNiCuAl) ； 鈍化

並列摘要

This study is to evaluate the corrosion resistance of the newly developed Fe-Co-Ni-Cu-Al high entropy alloy (HEA) in 3.5% NaCl solutions. Three corrosion inhibitors(Na3PO4、Na2MoO4 and NaNO2) were chosen to improve the corrosion resistance in test solutions. The results indicated that Na3PO4 exhibited the best corrosion inhibition efficiency among the test inhibitors due to improving the passivity region and reducing the passivation current in polarization curves.

並列關鍵字

Corrosion inhibitors ； High entropy alloy (HEA) ； Passivity