並列摘要
In this study, the doping method was used in organic thin-film transistors based on pentacene to increase the mobility of organic thin film. The two layers structure was adopted in this study like Fig. 1. Nitrogen was used as dopant added in the doping layer at room temperature and 70℃ respectively. The mobility of devices with nitrogen doping layer was enhanced by two and four times at room temperature and 70℃ respectively than ones without doping layer. Although the mobili ty was enhanced by nitrogen doping, the ratio of on/off current was decreased with adding dopant. The best mobility of the devices was 0.69cm^2/V(superscript *)s which was doped at 70℃.
並列關鍵字
無資料延伸閱讀
- 吳柏潭、蘇炎坤（2004）。Organic Thin-Film Transistors Based on Pentacene。真空科技，17(1)，39-43。https://doi.org/10.29808/JVSROC.200407.0006
- 陳逸銘（2007）。Organic thin film transistor〔碩士論文，國立臺灣大學〕。華藝線上圖書館。https://doi.org/10.6342/NTU.2007.01350
- 簡榮宏、葉安祺、陳存仁（2005）。Organic Thin Film Transistor Materials and Devices。化學，63(2)，241-249。https://doi.org/10.6623/chem.2005019
- Chuang, K. J. (2016). Amorphous InGaZnO Thin-Film Transistors with Vertical Channel Structure [master's thesis, National Chiao Tung University]. Airiti Library. https://www.airitilibrary.com/Article/Detail?DocID=U0030-0803201714392786
- Wang, C. H. (2012). Flexible organic thin film transistors with silk fibroin as gate dielectric [doctoral dissertation, National Tsing Hua University]. Airiti Library. https://www.airitilibrary.com/Article/Detail?DocID=U0016-0908201218153427