This study is divided into two parts: resin emulsification and effects of waterborne pressure sensitive adhesive (PSA) of mechanical properties. By controlling resin emulsion of particles size and zeta potential of increased two phase solubilization effect, then testing mechanical properties of PSA tape. The results showed that at pH 9, the Zeta potentials of the resin emulsion and PSA were -61.48mV and -83.45mV, respectively. The emulsion formula is physically stable, and there is no delamination even under high-speed centrifugation at 3000 rpm. The peel strength and shear strength of PSA tape were increased by 35.5% and 48.75%, respectively, indicating that the limiting viscosity of the polymer was higher. The cohesion is increased by 30%, indicate that no glue remains on the substrate when the tape is removed. The viscosity is increased by 90%, because of higher water retention helps the polymer molecules diffuse to the substrate, it causes better fast adhesion.