Laboratory Investigation on Performance of Cement Using Different Additives Schemes to Improve Early Age Compressive Strength
並列摘要
It is essential to maintain the oil well cement integrity effectively and economically. The classical literature review of cement slurry preparation has shown high temperature in wellbore has influenced the mechanical properties of cement slurry, especially compressive strength. The compressive strength is the most important parameter when the ability of the cement to perform its necessary functions of down-hole faster placement analyzed. In past, the different additives were used to improve the performance of cement slurry by maintain compressive strength during placement. Laboratory tests carry out by Silica Fume (SF) with dispersants and fluid loss control additives at different concentrations to performed early age compressive test of nondestructive cement slurry through Ultra-Sonic Cement Analyzer (UCA). Measured result showed that 6:34 and 7:48 h aged sample have a maximum compressive strength at temperature above 120℃. It is observed that as concentration of SF increased with combined dispersants and fluid loss additives used to control& enhance compressive strength at above 120℃ for the integrity of cement slurry.
延伸閱讀
- 郭俊志、江建豪、向性一、王建力（2013）。A Study of Physical and Chemicae Properties of the Corrosion Layer of API G Cements under Different CO2 Storage Environments Cement。鑛冶：中國鑛冶工程學會會刊，57(2)，87-93。https://doi.org/10.30069/MM.201306_57(2).0009
- Xu, S., Chen, J. W., Roggenkamp, C., & Zhang, W. (2019). Evaluating Bonding Agent's Effect in Microleakage of a Bioactive Restorative Material with Thermocycling and PH Challenge Test. 臺灣兒童牙醫學雜誌, 19(4), 133-142. https://doi.org/10.6319/TJPD.201912_19(4).0001
- 湛淵源、吳啟週、鄭凱維（2015）。Experiments: Sulfate Resistance and Anti-Corrosion for Concrete with Fly Ash, Granulated Blast-Furnace Slag and Slag Cement。建築學報，(91)，21-37。https://doi.org/10.3966/101632122015030091002
- Lu, C. C. (2018). Development of a suitable method for assessing the heavy metal leaching potential of incinerating recycled aggregate from bottom ash [master's thesis, National Taiwan University]. Airiti Library. https://doi.org/10.6342/NTU201802219
- Lin, S. K., Huang, C. H., Chang, C. S., Yen, T., Wu, C. H., & Lin, Y. (2010). Simultaneous Measurement of Deformation and Temperature of High-Strength Concrete at very Early Age to Determine the Initial and the Finial Setting Time. Journal of Marine Science and Technology, 18(2), 284-289. https://doi.org/10.6119/JMST.201004_18(2).0015