Corrosion Study of Pipeline Steel Weld Immersed in Sour Solution
並列摘要
This work presents an electrochemical study of API X52 pipeline steel weld immersed in NACE solution saturated with hydrogen sulphide (H_2S). The electrochemical techniques, polarization curves and linear polarization resistance are used in the corrosion test of the steel weld samples with the focus on the three different zones of the weldment, heat affected zone (HAZ), weld bead (WB) and base metal (BM). In addition, a brief analysis was made in order to identify the corrosion product film. It was found that the increment of temperature and H2S dissolved in the NACE solution increase the corrosion rate (CR) of the three different zones. HAZ was significantly affected by the corrosion test and the phases mackinawite, troilite and pyrrhotite were identified in the film of corrosion products.
延伸閱讀
- Tsai, T. M. (1995). Corrosion Behavior of JIS SS 41 Atmospheric Weldments and Underwater Weldments. 船舶科技, (16), 63-68. https://doi.org/10.30037/MT.199510.0005
- 陳文昌、陳國銘、曾立峰、趙健平（2014）。Corrosion Improvement of Circulation Loop Oil Process。防蝕工程，28(1)，27-38。https://doi.org/10.6376/JCCE.201403_28(1).0004
- 簡志宏、蔡育佑、黃燕飛、薛文景（2000）。Corrosion behaviors of welded AISI 304 stainless steels in 3.5% NaCl solution。防蝕工程，14(1)，37-43。https://doi.org/10.6376/JCCE.200003.0037
- 施建志、林葆喜（1992）。Corrosion Monitoring of Steel under Fireproofing Coating。防蝕工程，6(3)，25-31。https://doi.org/10.6376/JCCE.199209.0025
- Mohebbi, H., & Li, C. Q. (2011). Experimental Investigation on Corrosion of Cast Iron Pipes. International Journal of Corrosion, 2011(), 66-82. https://doi.org/10.1155/2011/506501