有機薄膜電晶體材料苯三併環噻吩及可溶性聯噻吩衍生物之開發

Synthesis of Soluble Organic Thin film transistors.

葉佳明(Chia-Ming Yeh)

指導教授 ： 陳銘洲

國立中央大學/理學院/化學系/碩士(2011年)

摘要

利用“one-pot” reaction 開發出不對稱主體苯三併環噻吩 (11)，其衍生物分子 (1) & (2) 已成功製備，兩者皆為 p-type 有機半導體材料，載子移動率利用真空蒸鍍製備分別達 0.026 及 9x10-4 cm2/Vs。可溶性聯噻吩主體的產率已順利提升，其衍生物 (3) ~ (9) 亦已成功開發，其中可溶性分子 (6)、(7)、(8) 皆展現不錯的載子移動率達 0.15、0.38 及 0.24 cm2/Vs。這些有機半導體材料皆表現相當良好的光、空氣與熱穩定性。

關鍵字

有機薄膜電晶體 ； 可溶性

並列摘要

Asymmetric fused thiophene compound (11) was synthesized by “one-pot” reaction. Based on compound (11), derivatives (1) and (2) have been developed. Both compounds exhibit p-type field-effect performances with mobility of 0.026 and 9x10-4 cm2/Vs via vacuum evaporation, respectively.
Compounds (3) ~ (9) have been successfully developed based on bithiophene compound (18). Preparation of soluble compound (18) has been improved with better yield. Compounds (6), (7), and (8) exhibit good field-effect performances with high mobility of 0.15, 0.38, and 0.24 cm2/Vs via solution process, respectively. All of these new semiconductor materials exhibit good stability under light, air, and thermal conditions.

並列關鍵字

organic thin film transistor

參考文獻

Tsumura, A.; Koezuka, K.; Ando, T. Appl. Phys. Lett. 1986, 49, 1210.

Street, R. A.; Salleo, A. Appl. Phys. Lett. 2002, 81, 2887-2889.

Ling, M. M.; Bao, Z. Chem. Mater. 2004, 16, 4824.

倪偵翔, 可溶性有機薄膜電晶體材料之開發, 國立中央大學化學研究所碩士論文, 2006.

江逸凡, 寡聚噻吩分子薄膜於不同基材表面的位向結構研究及其場效電晶體試製, 國立中央大學化學研究所碩士論文, 2006.