Grain-Boundary Magnetoresistance of CrO2 Films Grown on TiO2-Buffered LaAlO3 Substrates
並列摘要
The magnetic and magnetotransport properties of predominantly (110)-oriented CrO2 films grown on TiO2-buffered LaAlO3 substrates were investigated. The atomic force microscopic images revealed that the as-grown CrO2 films are granular. The magnetic measurements indicated that in-plane coercive fields are about 60 Oe and 100 Oe at 300 K and 7 K, respectively. The as-grown films are semiconductive below 75 K; a magnetoresistance with a △R/R0 ratio of -13 % in a magnetic field of 5 T was observed at 5 K, which is absent in high-quality epitaxial films. The coincidence between the coercive field and the peaks of the magnetoresistive loop measured at low temperatures indicates that spin-dependent scattering plays a crucial role in the transport properties.
並列關鍵字
無資料延伸閱讀
- Lee, M. H. (2018). Crystalline State and Domain Structure of Polycrystalline BiFeO3 Films Deposited by Radio-Frequency Magnetron Sputtering [master's thesis, National Tsing Hua University]. Airiti Library. https://www.airitilibrary.com/Article/Detail?DocID=U0016-0206202016112603
- 王玉富（2010）。Strain Effect on Anisotropic Magnetoresistance in La0.85Zr0.15MnO3 Epitaxial Films〔碩士論文，淡江大學〕。華藝線上圖書館。https://doi.org/10.6846/TKU.2010.00637
- 莊霈于（2012）。Magnetoresistance Property and Electronic Structure in Amorphous a-C:Co Films〔碩士論文，國立清華大學〕。華藝線上圖書館。https://doi.org/10.6843/NTHU.2012.00305
- 李佳璘（2009）。Anisotropic magnetoresistance in La0.85Zr0.15MnO3 thin films〔碩士論文，淡江大學〕。華藝線上圖書館。https://doi.org/10.6846/TKU.2009.00574
- Yao, H. (2005). Study of the giant electroresistance in epitaxial thin films of La0.9Sr0.1MnO3 [master's thesis, The University of Hong Kong]. Airiti Library. https://www.airitilibrary.com/Article/Detail?DocID=U0029-1812201200012250