Characterization and Aggregation of Silver Nanoparticles Dispersed in an Aqueous Solution

Colloidal solutions of silver nanoparticles were prepared by the chemical reduction method in which silver nitrate was used as a metal precursor and sodium citrate was used as a reducing as well as a stabilizing agent. UV-vis absorption spectra of the prepared colloids showed a surface plasmon resonance peak around 420 nm, indicating the formation of the nanoparticles. Size distribution analysis using a particle size analyzer showed that the average diameter of the synthesized nanoparticles is about 68 nm. This result was supported by the transmission electron microscope (TEM) images of the colloidal solutions. An X-ray diffraction (XRD) pattern was obtained to determine the crystalline structure of the silver nanoparticles. The aggregation of silver nanoparticles was investigated using different chemicals, mainly chlorides and hydroxides. These two categories of chemicals revealed different activity in the aggregating silver nanoparticles.

並列關鍵字

無資料

參考文獻

S. Schneider, P. Halbig, H. Grau, and U. Nickel, Photochem. Photobiol. 60, 605 (1994).

B. Teiten and A. Burneau, J. Colloid Interf. Sci. 206, 267 (1998).

P. C. Lee and D. Meisel, J. Phys. Chem. 86, 3391 (1982).

Y. Yin, Z. Li, Z. Zhong, B. Gates, Y. Xia et al., J. Mater. Chem. 12, 522 (2002).

Google Scholar

K. Song, S. Lee, T. Park, and B. Lee, Korean J. Chem. Eng. 26 153 (2009).

Google Scholar

被引用紀錄

Yang, H. Y. (2009). 無線隨意網路中以虛擬骨幹為基礎之路由協定 [doctoral dissertation, National Tsing Hua University]. Airiti Library. https://doi.org/10.6843/NTHU.2009.00049

張世杰（2012）。寬截止頻帶/可調式帶通濾波器與多頻天線設計〔碩士論文，國立中正大學〕。華藝線上圖書館。https://www.airitilibrary.com/Article/Detail?DocID=U0033-2110201613513138

國際替代計量

Characterization and Aggregation of Silver Nanoparticles Dispersed in an Aqueous Solution

全文下載

主題瀏覽