並列摘要
Zn(subscript 1-x)Mn(subscript x)Te(0≤x≤0.12) quantum dots (QDs) were grown on the Zn(subscript 1-y)Mn(subscript y)Se(0≤y≤0.05) buffer layer by alternating supplying and conventional molecular beam epitaxy (MBE). The formation of Zn(subscript 1-x)Mn(subscript x)Te QDs was confirmed by the atomic force microscopy (AFM) measurements and reflection high energy electron diffraction (RHEED) patterns. For the atomic smooth buffer layers, the Stranski-Krastanov (SK) growth mode was observed. On the other hand, the Zn(subscript 1-x)Mn(subscript x)Te QDs could also be grown by the Volmer Weber (VW) island growth mode on the rough buffer layer The shape of ZnTe QDs is cone shape with a typical radius of several tenths (10 to 50) nm and height of a few (1 to 8) nm. The dot density ranges from 10^8/cm^2 to 10^10/cm^2. The size distribution is found to be heavily tailed. The photoluminescence (PL) study showed that the band alignment of the Zn(subscript 1-x)Mn(subscript x)Te/Zn(subscript 1-y)Mn(subscript y)Se QD system is type Ⅱ. The carrier capture times were 7 and 38ps for the VW and SK ZnTe/ZnSe QDs.
並列關鍵字
無資料延伸閱讀
- 李偉新（2008）。Study For The Formation Mechanism In II-VI Semiconductor Nano Structure〔碩士論文，淡江大學〕。華藝線上圖書館。https://doi.org/10.6846/TKU.2008.00760
- 陳景祥（2009）。The Developed Situation of Nanoscience and Nanotechnology。華岡工程學報，(24)，1-9。https://doi.org/10.29987/CCUHKJE.200906.0001
- Cheng, C. T. (2005). Synthesis and Applications of Semiconductor Nanocrystallites [master's thesis, National Taiwan University]. Airiti Library. https://doi.org/10.6342/NTU.2005.00087
- Ng, M. C. (2007). Organic nanostructures [master's thesis, The University of Hong Kong]. Airiti Library. https://www.airitilibrary.com/Article/Detail?DocID=U0029-1812201200014241
- 楊登竣（2013）。Study For The Formation Mechanism Of II-VI Semiconductor Nanostructures.〔碩士論文，淡江大學〕。華藝線上圖書館。https://doi.org/10.6846/TKU.2013.00030