High Quality GaN Films Grown on Sapphire by RF-MBE without Low Temperature Buffer Layers
並列摘要
To improve the quality of grown GaN films, a low temperature (LT) buffer layer as a nucleation layer between GaN films and sapphire substrates is the most common way to solve the serve large lattice mismatch between GaN and sapphire. With a suitable Ga/N ratio, high quality GaN films can be grown directly on the sapphire without using any low temperature buffer layers by radio frequency molecular beam epitaxy (RFMBE). The 0.753 nm rms surface roughness and 5.4 arcmin full-width at the half-maximum (FWHM) of XRD can be achieved by optimizing the Ga/N ratio without any low temperature buffer layers. As shown in the results, the surface roughnesses and XRD FWHM of epilayers are a function of Ga flux at the same substrate temperature and N2 flow rate.
並列關鍵字
無資料延伸閱讀
- 王偉洲（2004）。Growth high quality GaAs thin film on Si substrates〔碩士論文，中原大學〕。華藝線上圖書館。https://doi.org/10.6840/cycu200400659
- 陳美汝、高慧玲（2012）。Characterization of Low Temperature Grown AlN Films on Sapphires Using Helicon Sputtering Method。清雲學報，32(3)，1-11。https://doi.org/10.7049/JCYU.201207.0001
- Wu, J. Y. (2008). High power GaN-Based HEMTs on Sapphire and Silicon Substrates [master's thesis, National Tsing Hua University]. Airiti Library. https://doi.org/10.6843/NTHU.2008.00173
- 潘羿明 (2013). Analysis of GaN Grown On Patterned Sapphire Fabricated by Nanosphere Lithography [master's thesis, National Tsing Hua University]. Airiti Library. https://doi.org/10.6843/NTHU.2013.00265
- Lee, W. C. (2009). MBE-grown High quality Oxide Thin Film for CMOS Technology beyond 16nm node [doctoral dissertation, National Tsing Hua University]. Airiti Library. https://doi.org/10.6843/NTHU.2009.00786