並列摘要
The pyrolysis and thermal behavior of Avgamasya (SE Anatolia, Turkey) asphaltite was performed using thermogravimetric analysis at atmospheric pressure in dynamic nitrogen atmosphere (30mL min^(-1)). Four heating rate profiles (2.5, 5, 10 and 20 K min^(-1)) were applied, with a final temperature 1123 K. Two-stage decomposition was observed in the experiments. During the stage 1, when the temperature is lower, only weaker chemical bonds are destroyed and some small gaseous molecules are produced. During the stage 2, when temperature is higher, the cracking is faster and stronger chemical bonds are broken, so that larger molecules decompose into small molecules in the gaseous phase. Kissinger (differential) and Coats-Redfern (integral) methods were applied to thermogravimetric data to obtain kinetic parameters (activation energy and Arrhenius constant).
並列關鍵字
無資料延伸閱讀
- 游瓊姿（2010）。The Study of Phase Transition and Synthesis of Thermal Sensitive Polymer〔碩士論文，國立臺北科技大學〕。華藝線上圖書館。https://www.airitilibrary.com/Article/Detail?DocID=U0006-1607201011490100
- Xia, Y. J., Xue, H. Q., Wang, H. Y., Li, Z. P., & Fang, C. H. (2011). Kinetics of Isothermal and Non-Isothermal Pyrolysis of Oil Shale. Oil Shale, 28(3), 415-424. https://www.airitilibrary.com/Article/Detail?DocID=17367492-201109-201111250020-201111250020-415-424
- Lin, Y. D. (2016). Improvement of thermal stability of thermoplastic polyether-ester elastomer [master's thesis, National Tsing Hua University]. Airiti Library. https://www.airitilibrary.com/Article/Detail?DocID=U0016-0901201710353691
- Kai-Tai Lu、Jin-Shuh Li、Tsao-Fa Yeh（2014）。The study of thermal stability for the single base propellant via the accelerated aging process。中正嶺學報，43(2)，69-78。https://www.airitilibrary.com/Article/Detail?DocID=P20221212001-N202303180014-00008
- 楊傑予（2002）。The relationship between thermal stability and refolding process of α-amylases〔碩士論文，中原大學〕。華藝線上圖書館。https://doi.org/10.6840/cycu200200467