Influence of Pretreatment on Cold Water Solubility and Esterification Activity of Starch
並列摘要
The aim of this study is to improve the Cold Water Solubility (CWS) and esterification activity of Native corn Starch (NS) by pretreatment NS using NaOH/urea aqueous solution. The influence of pretreatment on granule shape and crystal structure of corn starch was investigated by Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD). It has been found that the average particle size of Pretreatment corn Starch (PS) decreased to nanometer level, smaller than those of NS (4-15 μm). XRD revealed that crystalline pattern of PS was VH-type, which was different from that of NS (A-type). The maximum CWS of PS was 96.77%, while the NS was only 0.3%. NS and PS were esterified with oleic acid catalyzed by lipase under the same conditions respectively. The effects of the pretreatment on esterification activity of the corn starches were investigated by analyzing the Degrees of Substitutions (DS) of the esterification products. The maximum DS of pretreatment starch oleate was 0.229, while the DS of native starch oleate was very low and even could not be detected.
延伸閱讀
- 吳佳堯、施佩筠、賴秋君（2020）。Synthesis of Water-Containing PU Containing Stearyl Alcohol Anion and Application of Fabric Processing。紡織綜合研究期刊，30(1)，18-23。https://doi.org/10.6439/TTRJ.202001_30(1).0004
- Yeh, N. C. (2009). Investigation of Trichloroacetic Acid Biodegradation in Drinking Water Treatment Process [master's thesis, National Taiwan University]. Airiti Library. https://doi.org/10.6342/NTU.2009.01323
- 張家豪（2011）。Study of the Effect of Different Antiscalants on Membrane Distillation Performance〔碩士論文，中原大學〕。華藝線上圖書館。https://doi.org/10.6840/cycu201101035
- 黃俊智（2003）。Phenolic Wastewater Treatment by Chemical Precipitation and Resin Adsorption〔碩士論文，元智大學〕。華藝線上圖書館。https://www.airitilibrary.com/Article/Detail?DocID=U0009-0112200611322279
- Lai, X., Liu, J., Liu, G., Wang, L., & Ren, Q. (2019). Study on Synthesis and Thermal Stability of Non-amine Waterborne Polyurethane-polyacrylate. 淡江理工學刊, 22(1), 145-152. https://doi.org/10.6180/jase.201903_22(1).0014