Kinetics of chalcopyrite galvanic leaching using sulfate medium at low temperature in the Galvanox^(TM) process
摘要
In this research, the dissolution of chalcopyrite was investigated under atmospheric pressure, with a sulfate medium at low temperatures, in 30°C to 50°C. In the galvanic interaction between chalcopyrite and pyrite, pyrite is used as a leaching catalyst. Effects of different parameters such as temperature, stirring speed, pyrite to chalcopyrite ratio, particle size, and solution potential were examined. Results showed that maximum copper recovery in low temperature was achieved after 24 hours, under the following condition: stirring speed of 800rpm, pyrite to chalcopyrite ratio of 4, solution potential of 440mV, temperature of 50°C, and particle size of -38 microns. In addition, kinetic studies indicated that chalcopyrite dissolution with pyrite followed the shrinking core model, and the reaction was controlled by the surface reaction. Activation energy (Ea) was calculated as 88 kJ/mol.
延伸閱讀
- 陳正強、羅翊庭、劉竹峰、洪正聰、許能傑（2007）。Growth of Lanthanum Gallium Silicate Single Crystals by Czochralski Pulling Method。臺北科技大學學報，40(2)，41-47。https://doi.org/10.29768/JNTUT.200711.0004
- 郭于嫚（2008）。Effects of atmosphere of calcination on the formation of crystalline LaAlO3 derived from the citrate precursor method〔碩士論文，淡江大學〕。華藝線上圖書館。https://doi.org/10.6846/TKU.2008.00163
- Wang, Y. J. (2009). Extraction of 1,3-Propanediol from Aqueous Phase to Organic Phase Using Salting Out [master's thesis, Yuan Ze University]. Airiti Library. https://doi.org/10.6838/YZU.2009.00289
- Mehrabani, J., Shafaei, S. Z., Noaparast, M., & Mousavi, S. M. (2016). Bioleaching of a low grade sphalerite concentrate produced from tailings flotation. International Journal of Mining and Geo-Engineering, 50(2), 169-173. https://doi.org/10.22059/ijmge.2016.59825
- Khawassek, Y. M., E., A. E., Haggag, A., Mohamed, S. A., & Omar, S. A. (2016). Kinetics Leaching Process of Uranium Ions from El-Erediya Rock by Sulfuric Acid Solution. International Journal of Nuclear Energy Science and Engineering, 6(), 35-48. https://doi.org/10.14355/ijnese.2016.06.004