富鎳Ti49Ni51形狀記憶合金時效後之相變態與性能最佳化之研究

Transformation Characteristics and Properties Optimization of the Aged Ni-rich Ti49Ni51 Shape Memory Alloy

指導教授 : 吳錫侃

摘要


本研究針對Ti49Ni51 形狀記憶合金(SMA)之相變態、形狀記憶效應(SME)、超彈性(PE)與超彈性應力應變循環等性質之提升作一系列的探討。900℃×1hr固溶處理後之硬度值約為303HV。研究結果發現,一階段250℃時效者在25小時可達374HV之最大硬度。一階段時效於250℃、300℃及350℃等溫度,主要為B2↔R變態;而時效於400℃、450℃及500℃時,R相及B19’變態都非常明顯,由DSC結果可知上述之B2→R變態的RS溫度與反應熱都以300℃時效為最大。在300℃時效50小時者(硬度360HV)在SME及PE試驗中,其應力大於固溶處理者,殘留應變也較少,這是因為析出物強化基地,使塑性變形較不易產生所造成的。在二階段時效者中,其最大硬度值可達348Hv,雖然不及一階段時效者,但其SME之性能達100%,而在制振能的研究方面,發現二階段時效者相變態時之tanδ值相當高,可達0.073,僅次於固溶處理的試片,表示其比一階段時效者擁有良好的制振能。本研究之Ti49Ni51 SMA與Ti49.3Ni50.7者相比較,不論做一階段或兩階段時效者,發現Ni含量的增加對其SME及PE性能之改善是有顯著的效益,此因鎳含量提高,固溶強化及析出硬化的效果也增強。

並列摘要


In this study, the property improvement of shape memory effect (SME) and pseudoelasticity (PE) exhibited in Ni-rich Ti49Ni51 shape memory alloy (SMA) solid-soluted(SS) and aged at 250℃~500℃ for various time is investigated. The hardness of specimen at 900℃x 1 hr SS and water quenched is 303HV. Among all aged specimens, the maximum hardness is 374 HV for specimen aged at 250℃x25 hrs. From DSC tests, B2↔R transformation mainly appears in specimens aged at 250℃~350℃, but both B2↔R and R↔B19’/B2↔B19’ transformations occur in specimens aged at 400℃~500℃. The Rs temperature and ∆HR value of B2↔R transformation reach their maxima for specimens aged at 300℃. In the early aging, the curve of the specimen hardness at room temperature v.s. aging time has the 1st maximum, the minimum and the 2nd maximum , in which the 2nd maximum is also the highest hardness possessed in aged alloy. From DSC results and TEM observations, the formation of R phase and nano-precipitates is closely related to the hardness maximum and minimum exhibited in specimens aged at 250℃~400℃. The specimens with two step aging have 100% SME and higher damping capacity even though their the maximum hardness is 348HV. The tensile tests for specimens aged at 300℃x50 hrs (hardness 360HV) and at 250℃x5 hrs+400℃x1 hr (hardness 341HV) indicate their SME and PE properties are better than those of Ti49.3Ni50.7 due to the former has higher SS strengthening and precipitation hardening.

參考文獻


[87] 林世庭, 國立台灣大學材料科學與工程學研究所碩士論文, (2010) 台北。
[88] 張國祥, 國立台灣大學材料科學與工程學研究所碩士論文, (2011) 台北。
[86] 林耿華, 國立台灣大學材料科學與工程學研究所碩士論文, (2009) 台北。
[6] K. Otsuka, K. Shimizu, International Metals Reviews, 31 (1986) 93.
[22] T. Tadaki, Y. Nakata, K. Shimizu, K. Otsuka, Trans. JIM, 27 (1986) 731.

被引用紀錄


匡載訢(2015)。時效對富鎳Ti48Ni52及Ti48.5Ni41.5Cu10形狀記憶合金相變態影響之研究〔碩士論文,國立臺灣大學〕。華藝線上圖書館。https://doi.org/10.6342/NTU.2015.01053
李宗縉(2014)。鈦鎳矽三元形狀記憶合金之研究〔碩士論文,國立臺灣大學〕。華藝線上圖書館。https://doi.org/10.6342/NTU.2014.00455
何建陞(2013)。富鎳Ti48.7Ni51.3及Ti48.4Ni51.6形狀記憶合金時效後之相變態與性能之研究〔碩士論文,國立臺灣大學〕。華藝線上圖書館。https://doi.org/10.6342/NTU.2013.00716

延伸閱讀