Comparison of One-Zone and Two-Zone Thalliation Processes in the Tl2Ba2CaCu2Ox Superconducting Thin Films
並列摘要
Superconducting Tl2Ba2CaCu2Ox, (2212) thin films have been prepared on (110) MgO substrates using ex-situ one-zone and two-zone thalliation processes. The Tl2O vapour pressure was adjusted by either thalliation temperature (one-zone method; or the position of the thallium source (two-zone method). The thalliation conditions were set between 830 and 880℃ with various periods of time. Thalliated Tl2Ba2CaCu2Ox films with Tc0 values of around 102 K and Jc (77 K) up to 5 x 10^5 A/cm^2 have been obtained. On consideration of controlling thallium vapour pressure, we find that the two-zone thalliation process is relatively simple and straight forward. which can be very helpful for controlling grain structure.
並列關鍵字
無資料延伸閱讀
- Chen, H. A. (2014). Effect of Bias on the Structure and Properties of TiZrN Thin Films Deposited by Unbalanced Magnetron Sputtering [master's thesis, National Tsing Hua University]. Airiti Library. https://www.airitilibrary.com/Article/Detail?DocID=U0016-2912201413524144
- Lin, Y. W., Lu, C. W., Yu, G. P., & Huang, J. H. (2016). Structure and Properties of Nanocrystalline (TiZr)_xN_(1−x) Thin Films Deposited by DC Unbalanced Magnetron Sputtering. Journal of Nanomaterials, 2016(), 673-684-071. https://doi.org/10.1155/2016/2982184
- Chen, P. N. (2010). Preparation and post-annealing of ZrCuAgAl thin films by unbalanced magnetron sputtering [master's thesis, National Tsing Hua University]. Airiti Library. https://doi.org/10.6843/NTHU.2010.00579
- Qian, P., Shen, J., & Chen, N. X. (2013). Phase Stability, Site Preference, and Mechanical Properties of Th2Co6Al19 and U2Co6Al19. Chinese Journal of Physics, 51(2), 388-396. https://doi.org/10.6122/CJP.51.388
- Chen, J. M., Liu, R. G., Liu, R. S., Lin, H. C., Uen, T. M., Juang, J. Y., & Gou, Y. S. (1998). Polarized X-ray Absorption Studies in Double-Thallium-Layer Superconducting. Chinese Journal of Physics, 36(2S), 330-335. https://www.airitilibrary.com/Article/Detail?DocID=05779073-199804-201211010025-201211010025-330-335