紫外光可交聯型疏水性PU樹脂製備及其鋼材防蝕和撥水織物應用研究

Preparations of UV-curable Hydrophobic PU Resins for Steel Corrosion Control and Water-repellent Textile Applications

指導教授 : 陳幹男

摘要


本論文開發一系列疏水性紫外光可硬化型高分子樹脂分別於鋼材防蝕和織物撥水之功能化塗裝技術。 鋼材防蝕: 首先將含磷酸酯基之紫外光硬化型環氧樹脂(UV EPOXY- POH)與紫外光硬化型矽氧烷(TMSPMA)依一定比例混摻當冷軋鋼片底漆;另外,將含氟素、含長碳鏈或含聚二甲基矽氧烷之紫外光硬化型PU預聚物當疏水性面漆,利用紫外光硬化機照射而形成緻密的疏水性能性防蝕保護塗層。此系列的加工後的鋼片其百格測試為4B以上,鉛筆硬度可達4H,而且經鹽霧試驗證明此研究成果具有可耐148小時以上的抗腐蝕能力。 織物撥水: 分別將含氟素、含長碳鏈和含聚二甲基矽氧烷之紫外光硬化型PU預聚物依一定比例混摻,運用織物浸漬(Dipping)的加工方式將功能性PU塗佈在聚酯(PET)織物,並利用紫外光照射產生架橋硬化反應,形成具有化學鍵結的互穿式網狀交聯(IPN)系統,不僅可以崁入織物纖維之間,更可將高度架橋PU樹脂使其固定在織物纖維間,進而提高PET織物的耐水洗性。紫外光硬化型PU在最適加工條件下,經撥水加工後的織物其對水的接觸角可以達到超過140°以上,且經過AATCC標準20次洗滌後仍能維持其原有的撥水效果(接觸角140°以上),故證實此研究成果可應用於長效性的撥水加工織物的應用。

關鍵字

防蝕 環氧樹脂 紫外光交聯 撥水 聚胺酯

並列摘要


This research has been developed a series of hydrophobic UV curable polymeric materials for steel corrosion control as well as water-repellency applications. Steel corrosion control coat: A phosphate-containing UV-curable coating system is obtained by blending epoxy (UV EPOXY-POH) and UV-curing siloxane (TMSPMA) in various ratios as a steel base coat; In addition, a hydrophobic group (fluorine-, long chain hydrocarbons or polydimethylsiloxane) -containing UV-curing PU prepolymer has been applied on top of steel primer as a top coat after UV-curing. The primer coat provides the tough (4H pencil hardness) with excellent adhesion (cross-cut passes 4B) surface and the top coat has been providing hydrophobic and dense protective surface coating. Furthermore, these steel anti-corrosion coatings have been standing for more than 148 hours salt spray test. Water-repellent Textile treatment: A mixture with various ratios of these hydrophobic groups-containing UV-curing PU prepolymers has been prepared for water-repellent textile treatment. A PET textile has been treated with these hydrophobic PU prepolymer by dipping process and then cured by UV-radiation. A water-repellent PET textile has resulted and that demonstrated by its contact angle reaches to 140o on treated textile surface. And its contact angle has been remained after 20 water washing cycles (AATCC method). Due to UV-curing process creates IPN (interpenetrating networks of hydrophobic PU) within textile fibers that enhancing the washing durability.

並列關鍵字

Anti-Corrosion Epoxy UV-Curing Water Repellency Polyurethane

參考文獻


7. 陳威宏, 高分子材料應用在功能化塗裝之研究開發, 淡江大學化
13. 郭勇, 鍍鋅鋼片之耐蝕性與上漆性評估介紹, 防蝕工程, 1995.
14. 葉錫宜, 記憶金屬表面之血栓調節束固定化及其生活物性及血液相容性之研究, 成功大學化學與工程學系碩士論文, 2002.
10. 陳依湘, 環氧樹酯/二氧化矽混成材料之製備及其在金屬防蝕上
53. 王惠君, 以回應曲面法探討 Sol-Gel 製備奈米二矽之參數影響,

被引用紀錄


李宇翔(2013)。有機/無機複合材料應用於金屬保護塗膜研究〔碩士論文,淡江大學〕。華藝線上圖書館。https://doi.org/10.6846%2fTKU.2013.01144
陳竹軒(2013)。以水性聚胺酯為基底引入壓克力多元醇及二氧化矽 合成可熱交聯之抗腐蝕塗料〔碩士論文,國立臺灣大學〕。華藝線上圖書館。https://doi.org/10.6342%2fNTU.2013.03033

延伸閱讀