Title

電化學製備MgO薄膜在純鎂基材上提升在NaCl溶液中之抗腐蝕性

Translated Titles

Preparing Mgo Thin Film on Pure Magnesium for Increasing Corrosion Resistance in NaCl Solution by Electrochemical Method

DOI

10.6845/NCHU.2013.00416

Authors

許茂成

Key Words

電化學合成 ; 陰極極化曲線 ; 沉積機構 ; Mg(OH)2 ; MgO ; 抗蝕性 ; Electrochemical synthesis ; cathodic polarization curves ; deposition mechanism ; Mg(OH)2 ; MgO ; corrosion resistance

PublicationName

中興大學材料科學與工程學系所學位論文

Volume or Term/Year and Month of Publication

2013年

Academic Degree Category

碩士

Advisor

顏秀崗

Content Language

英文

Chinese Abstract

本研究是藉由電化學沉積MgO鍍層在純鎂基材上應用於防制腐蝕。經由X光繞射(XRD)分析與SEM觀察,顯示經由電解反應可形成Mg(OH)2鍍層,再經370℃退火可形成MgO,其中Mg(OH)2鍍層結晶取向與施加的電壓有關,主要是由於在較負的電壓下,會有較多的OH-離子產生,造成鍍層會有(001)的從優取向。因此我們可以藉由不同的電位來控制Mg(OH)2鍍層的表面形貌。經由電化學極化分析與浸置實驗,可知沉積電位-2.0 V,鍍膜時間2400s,400℃退火處理有較均勻致密的MgO鍍層,且在3.5wt %的NaCl溶液中腐蝕電流由114降低到5.82 μA/cm2,鈍化區域從-1.72到 -1.57 V(Ag/AgCl),可有效改善純鎂的抗蝕性而與微弧氧化法(MAO)性能相當。

English Abstract

The electrolytic MgO coating on Mg alloy has been carried out in 0.1 M Mg(NO3)2 aqueous solution to improve its corrosion resistance. By X-ray diffraction (XRD), and scanning electron microscopy (SEM),the as-deposited film was Mg(OH)2 formed by the electrolysis, (Mg2+•2H2O → Mg(OH)2 + H2) , and finally condensed into MgO at 370 ℃. It was also found that the crystal orientation and morphology of Mg(OH)2 was linked to the applied voltage. The more negative the applied voltage and the more the OH- concentration was, finally resulting in the more (001) preferred orientation and various related surface appearances. Therefore, the controllable fabrication of highly dense and uniform Mg(OH)2 film could be carried out by tuning deposition potential. An optimum process conducted at -2.0 V(Ag/AgCl) for 2400s and annealed at 400 ℃ was suggested to derive a more uniform and densified MgO protective film, revealing corrosion current density reduced from 114 down to 5.82 μA/cm2 and a passivation region from -1.72 to -1.57 V(Ag/AgCl) in 3.5 wt% NaCl aqueous solution, comparable with micro-arc oxidation.

Topic Category 工學院 > 材料科學與工程學系所
工程學 > 工程學總論
Reference
  1. [7] Y. Kojima, Mater. Sci. Forum 350–351 (2000) p. 3.
    連結:
  2. [11] B.L. Mordike and T. Ebert, Mater. Sci. Eng. A302 (2001) p. 37.
    連結:
  3. [14] G. Song, A. Atrens, Corrosion mechanisms of magnesium alloys, Advanced Engineering Materials 1 (1999) p. 11.
    連結:
  4. [16] O. Lunder, T.K.R. Aune, K. Nisancioglu, Effect of Mn additions on the corrosion behaviour of mould-cast magnesium ASTM AZ91, Corrosion 43 (1987) p. 291.
    連結:
  5. [17] O. Lunder, J.E. Lein, T.K.R. Aune, K. Nisancioglu, The role of the Mg17Al12 phase in the corrosion of Mg alloy AZ91, Corrosion 45 (1989) p. 741.
    連結:
  6. [18] J. D. Hanawalt, C. E. Nelson, and J. A. Peloubet, Corrosion studies of Magnesium and Its Alloys, Trans. AIME, 147 (1942) p. 273.
    連結:
  7. [19] G. Song, A. L. Bowles, D. H. StJohn, Materials Science and Engineering A366 (2004) p. 74.
    連結:
  8. [20] N.N. AUNG, W. ZHOU, Journal of Applied Electrochemistry, 32 (2002) p. 1397.
    連結:
  9. [21] Y. Li , T. Zhang, F. Wang, Electrochimica Acta 51 (2006) p. 2845.
    連結:
  10. [24] T. Okuma, Magnesium and bone strength, Nutrition 17 (2001) p. 679.
    連結:
  11. [25] J. Vormann, Magnesium: nutrition and metabolism, Mol Aspects Med 24 (2003) p. 27.
    連結:
  12. [26] F.I. Wolf and A. Cittadini, Chemistry and biochemistry of magnesium, Mol Aspects Med 24 (2003) p. 3.
    連結:
  13. [27] A. Hartwig, Role of magnesium in genomic stability, Mutat Res/Fund Mol Mech Mutagen 475 (2001) p. 113.
    連結:
  14. [31] S. H. C. Liang and I. D. Gay, J. Catal. 101(1986) p. 293
    連結:
  15. [35] H. Duan, K. Du, C. Yan, F. Wang, Electrochem. Acta, 51 (2006) p. 2898.
    連結:
  16. [37] L. Gibson and M. Ashby, Cellular solids. Structure and properties, Pergamon Press, Sydney (1988) p. 1.
    連結:
  17. [38] L. Gibson and M. Ashby, Cellular solids. Structure and properties, Pergamon Press, Sydney (1988) p. 316.
    連結:
  18. [39] J.W. Choi, Y.M. Kong, H.E. Kim and I.S. Lee, Reinforcement of hydroxyapatite bioceramic by addition of Ni3Al and Al2O3, J Am Ceram Soc 81 (1998) p. 1743.
    連結:
  19. [42] G. L. Makar and J. Kruger, Int. Mater. Rev., 38, 138 (1993).
    連結:
  20. [1] Emission Control, Automotive World 4 (2000) p. 10.
  21. [2] T. Gill, “Automobiles drive growth in secondary magnesium”, Metal Bulletin Monthly 314 (1997) p. 63.
  22. [3] J. Davis, SAE Technical Paper 910551, Detroit, MI, 1991.
  23. [4] C. Akey, J Davis, In: Magnesium: The Performance Material, Internattion Magnesium Association, Dearborn, MI, (1989) p. 1.
  24. [5] S. Schumann, F. Friedrich, in: B. Mordike, K. Kainer (Eds.), Material Alloys and their Application, Werkstoff-Informationsgesellschaft mbH, Wolfsburg, Germany, (1998) p. 3.
  25. [6] G. Cole, in: Magnesium into the Next Millenium, International Magnesium Association, Rome, Italy, (1999) p. 21.
  26. [8] D.V. Hai, S. Itoh, S. Kamado and Y. Kojima, Adv. Mater. Res. 11-12 (2006) p. 413.
  27. [9] S. Schumanm and H. Friendich, Mater. Sci. Forum 419-422 (2003) p. 51
  28. [10] L.L. Rokhlin, Magnesium Alloys Containing Rare Earth Metals-Structure and Properties (Taylor & Francis Pub., Moscow, (2003) p. 83.
  29. [12] M.M. Avedesian, H. Baker, Magnesium and Magnesium Alloys — ASM Speciality Handbook, ASM International, Ohio, (1999) p. 1-71.
  30. [13] D.A. Jones: Principles and Prevention of Corrosion, 2nd ed., Prentice Hall, Englewood Cliffs, NJ, (1996) p. 40
  31. [15] G.L. Makar, J. Kruger, Corrosion of magnesium, International Materials Reviews, 38 (1993) p. 138.
  32. [22] Water, electrolyte mineral and acid/base metabolism. Section 2. Endocrine & Metabolic Disorders. Merk Manual of Diagnosis and Therapy Chapter 12
  33. [23] N.E.L. Saris, Magnesium: an update on physiological, clinical and analytical aspects, Clin Chim Acta 294 (2000), pp. 1
  34. [28] M. Staiger, A. Pietak, J. Huadmai, G. Dias, Biomater. 27 (2006) p. 1728.
  35. [29] B. Heublein, R. Rohde, V. Kaese, M. Niemeyer,W. Hartung,W. Haverich, Heart 89 (2003) 651.
  36. [30] Ph. Baranek, A. Lichanot, R. Orlando, R. Dovesi, Chemical Physics Letters 340 (2001) p. 362
  37. [32] Y. Ding, G. Zhang, H. Wu, B. Hai, L. Wang and Y. Qian, Chem. Mater. 13 (2001) p. 435
  38. [33] F. Stippich, E. Vera, G. K. Wolf, G. Berg, C. Friedrich, Surf. Coat. Tech., 103-104 (1998) p. 29.
  39. [34] WebElements. "Chemistry : Periodic Table : compound data [magnesium (II) oxide". Retrieved on 2008-12-06.
  40. [36] P.E. DeGarmo, Materials and processes in manufacturing (5th ed), Collin Macmillan, New York (1979).
  41. [40] T.V. Thamaraiselvi and S. Rajeswari, Biological evaluation of bioceramic materials—a review, Trends Biomater Artif Organs 19 (2004) p. 9.
  42. [41] C. F. Li, W. H. Ho, and S. K. Yen, J. Electrochem. Soc., 156, E29 (2009).
  43. [43] Z. Koren, H. Rosenson, E. M. Gutman, Ya. B. Unigovski, and A. Eliezer, J. Light Met., 2, 81 (2002).
  44. [44] Y. Wang, G. Liu, and Z. Fan, Scr. Mater., 54, 903 (2006)
  45. [45] W. Mu, Y. Han, Surface and Coatings Technology, 202 (2008) p. 4278
  46. [46] J. Slunecko, M. Kosec, J. Holc, G. Drazic, J. Am. Ceram. Soc. 81 (1998) p.1269..