聚苯胺與聚噻吩衍生物/奈米碳材複合材料之合成與電學性質研究

劉錚達

3.236.175.108，Hello！

Close
Search Quick Search Advanced Search Publication Search	Personal Service Member Login Searching History Use Bonus Card SYMSKAN
Browse Browse by University of Graduate Thesis Browse by Pinyin of Graduate Thesis Browse by Conference Proceedings Topic Browse by Conference Proceedings Publisher Browse by Pinyin of Conference Proceedings Browse by eBook Category Browse by eBook Topic Browse by eBook Publisher
Customer Services Authorize Airiti Recommend a Journal

Search Symbol (Half-width)	Description of Search Symbols
Space	"AND" indicates the intertwining of key terms used in a search
Double Quotation Marks ("") ( " " )	Double quotation marks indicate the beginning and end of a phrase, and the search will only include terms that appear in the same order of those within the quotations. Example: "image process" ： " image process "
?	Indicates a variable letter. Entering two ? will indicate two variable letters, and so on. Example: "Appl?", search results will yield apple, apply… e , appl y … ( (often used to English word searches) )
*	Indicates an unlimited number of variable letters to follow, from 1~n. Example: Enter "appl*", search results will yield apple, apples, apply, applied, application…(often used in English word searches) e , appl es , appl y , appl ied , appl ication … ( (often used to English word searches) )
AND、OR、NOT	Boolean logic combinations of key words is a skill used to expand or refine search parameters. (1) AND (1) AND: Refines search parameters (2) OR (2) OR: Expands search parameters (3) NOT: Excludes irrelevant parameters

DOI stands for Digital Object Identifier （ D igital O bject I dentifier ） ,
and is the unique identifier for objects on the internet. It can be used to create persistent link and to cite articles.

Using DOI as a persistent link

To create a persistent link, add「http://dx.doi.org/」「 http://dx.doi.org/ 」 before a DOI.
For instance, if the DOI of an article is 10.5297/ser.1201.002 , you can link persistently to the article by entering the following link in your browser: http://dx.doi.org/ 10.5297/ser.1201.002 。
The DOI link will always direct you to the most updated article page no matter how the publisher changes the document's position, avoiding errors when engaging in important research.

Cite a document with DOI

When citing references, you should also cite the DOI if the article has one. If your citation guideline does not include DOIs, you may cite the DOI link.

DOIs allow accurate citations, improve academic contents connections, and allow users to gain better experience across different platforms. Currently, there are more than 70 million DOIs registered for academic contents. If you want to understand more about DOI, please visit airiti DOI Registration （ doi.airiti.com ）。

Data Source

College of Engineering > Graduate Institute of Polymer Science and Engineering
Engineering > Chemical Industry

Bibliography Management Tool

Related Links

Report an Issue

Search in Library

There is no full-text available at the moment. Airiti would like to request author's authorization. I would like to provide authorization.

聚苯胺與聚噻吩衍生物/奈米碳材複合材料之合成與電學性質研究

Synthesis and electrical properties of Polyaniline and Polythiophene derivatives/Nano-carbon composites

劉錚達 , Ph.D　　Advisor：謝國煌　　

英文

聚苯胺；聚噻吩；奈米碳管；光阻劑；電磁波屏蔽； polyaniline ； polythiophene ； photoresist ； multi-wall carbon nanotube ； electromagnetic interference (EMI) shielding

Abstract │ Reference (162) │ Altmetrics

Abstract 〈TOP〉

本研究合成聚苯胺與聚噻吩衍生物製備導電性奈米碳管複合材料探討其導電性、電磁波屏蔽與其他光電性質。第一部分我們以乳化聚合法合成奈米級聚苯胺粒子，並採用本實驗室自行開發之absorption-transferring process，使之分散於環氧樹脂中。Absorption-transferring process 是以苯胺聚合雙酚A系列之環氧樹脂(DGEBA)為母體，利用其加熱後之黏滯性在水相媒介中吸附懸浮之奈米顆粒。其優點可避免奈米粒子聚集且不需任何有機溶劑。由掃描式電子顯微鏡分析聚苯胺/環氧樹脂材料，可明顯觀察出奈米級聚苯胺顆粒均勻分散在母體中，觀察不到大規模聚集的現象。利用阻抗分析儀量測其介電行為並呈現負介電常數現象，可推斷該材料呈現出巨觀的電荷未定域化現象。使用電磁波屏蔽測試，均勻分散的聚苯胺/環氧樹脂材料在100~1000MHz的電場頻率範圍最高可達到30~60dB的屏蔽效果。在導電薄膜部份，我們合成含壓克力與氫氧官能基之環氧樹脂為光阻劑，經過曝光顯影製程不同線寬圖形，再利用光阻劑表面之氫氧基與2, 4-Toluene diisocyanate(TDI)反應後接上3-Methyl-3,4-dihydro-2H-thieno[3,4-b]dioxepin-3-yl)methanol (ProDOT-OH)單體，再將薄膜浸泡入水中，加入3-thienyl ethoxybutanesulfonate (TEBS)與三甲苯磺酸鐵進行共聚反應，製得導電薄膜。在PET基板上之軟性導電薄膜其圖形解析度(line widths/spaces)為100μm/100μm與10μm/5μm，最佳導電度為90 S/cm，可見光範圍之透明度達70%。而材料之導電性與圖形線寬、聚合時間均有所影響。最後我們亦合成低能隙高分子製備奈米碳管與碳球複合材料討論有機半導體之光電特性。Poly(3,4-dihexyloxythiophene) (PDHOT) and poly(3,4-dimethoxythiophene-co- 3,4-dihexyloxythiophene) [P(DMOT-co-DHOT)] 以紫外光-可見光譜分析儀判定其能隙約為1.34~1.38 eV之間，並以之與官能化奈米碳管混掺，得到分散均勻之奈米碳管/低能隙高分子複合材料。由掃描式電子顯微鏡觀察，當官能化奈米碳管含量高達20wt%，奈米碳管仍均勻分散在母體中觀察不到明顯大規模聚集。此外，我們將PDHOT和P(DMOT-co-DHOT)與奈米碳球(PCBM)混合製備太陽能電池元件，檢測其光電性質。

Parallel Abstract 〈TOP〉

In this study, we prepared different conducting polymer and carbon nanotube composites including polyaniline nano-particle, polythiophene derivative and MWNT/PANI core-shell material to discuss their conductivity, EMI shielding efficiency and optoelectrical properties.
First section, novel polyaniline (PANI)/epoxy hybrids have been fabricated using an absorption-transferring process in which no organic solvent is involved. An epoxy prepolymer cured by aniline monomer (DGEBA-aniline) was added to a freshly prepared PANI nanoparticles (NPs) aqueous solution with vigorous agitation and heating (ca. 90 C). The PANI NPs were
absorbed on the surface of epoxy droplet and then transferred into the whole droplet. The
microstructures of the product PANI/epoxy hybrids, characterized using scanning electron
microscopy, featured well-dispersed PANI NPs (ca. 40□60 nm) within epoxy matrixes; no large
aggregates were observed. The hybrids exhibited huge negative permittivities; the electromagnetic
interference shielding efficiency in an electric field at low frequency (100-1000 MHz) was ca.
30-60 dB. The well dispersed PANI NPs not only provided a continuous conducting network but
also a higher level of charge delocalization. On other hand, we also synthesized MWNT/PANI
core-shell (MPCS) structure, it could also dispersed in DGEBA-Ani through
absorption-transferring process.
In the section of conducting patterned film, A UV-curable photoresist containing hydroxyl
groups has been prepared from a mixture of a photoinitiator, epoxy-acrylate resin, hydroxyethylmethacrylate, and tripropylene glycol diacrylate. Patterns having line widths/spaces of 100/100 μm
and 10/5 μm were fabricated on a PET (Polyethylene terephthalate) substrate using lithography
techniques. 3-Methyl-3,4-dihydro-2H-thieno[3,4-b]dioxepin-3-yl)methanol (ProDOT-OH) was
self-synthesis through urethane-linkages onto the surface of the patterned photoresist on the PET
film, which was then dipped into a solution of the other monomer, 3-thienyl ethoxybutanesulfonate
(TEBS), and initiator and in situ–polymerized to form conductive poly(ProDOT-OH-co-TEBS)
films covering the surface of the patterned resist. The optimal conductivity of the
poly(ProDOT-OH-co-TEBS) film was ca. 90 S/cm with an optical transparency of ca. 70%. The
conductivity of the film was controlled by the polymerization reaction time and the resolution of
the pattern. These conductive patterned films might be applicable to the manufacture of industrial
touch panels or chemical/biological sensors.
Finally, we prepared nanocomposites of multi-wall carbon nanotubes (MWNTs) and
low-energy-bandgap conjugated polymers incorporating 3,4-alkoxythiophene monomers.
Poly(3,4-dihexyloxythiophene) (PDHOT) and
poly(3,4-dimethoxythiophene-co-3,4-dihexyloxythiophene) [P(DMOT-co-DHOT)] have relatively
low energy bandgaps (ca. 1.38 and 1.34 eV, respectively), determined from the onsets of
absorbances in their UV–Vis spectra, because of the electron donating effects of their alkoxy
groups. MWCNTs have poor solubility in common organic solvents; after surface modification
with alkyl side chains using the Tour reaction, however, the MWCNT-HA derivatives were readilydispersed in CHCl3 and could be mixed with the low bandgap polymers. Scanning electron
microscopy images revealed that MWCNT-HA was dispersed well in each polythiophene
derivative; only a few MWCNT-HA bundles could be observed at a high MWCNT-HA content (＞
20 wt%). The electrical conductivities of the MWCNT/PDHOT composites were dependent on
their MWNT contents, reaching 16 S/cm at 30 wt% MWCNT-HA. We suspect that the two
hexyloxy chains of PDHOT enhanced its solubility and allowed it to wrap around the surfaces of
the MWCNTs more readily.

Reference ( 162 ) 〈TOP〉

[2] R. H. Norman, Conductive rubbers and Plastics, Elsevier, Amsterdam, 1970
連結：
[4] F. Carmona, Physica A, 1989, 157, 461
連結：
[5] M. Armand, Adv. Mater., 1990, 2, 278
連結：
[10] M. Kertez, J. Koller, A. Azman, J. Chem. Phys., 1977, 67, 1180
連結：
[12] Y. S. Lee, M. Kertesz, J. Chem. Phys., 1988, 88, 2609
連結：

Altmetrics

〈TOP〉

E-mail ：

When an article is available to download, a notice will be sent to your mailbox address.

E-mail ：