Enhancement of Type-I Emission in Type-Ⅱ Zn0.97Mn0.03Se/ZnSe0.8Te0.2 Quantum Wells under Applied Electric Field
並列摘要
In this study, multiple quantum well (QW) structures were formed by the diluted magnetic semiconductor, Zn0.97Mn0.03Se, and ZnSe0.8Te0.2 using molecular beam epitaxy. The thickness of ZnSe0.8Te0.2 layer was changed from 1, 2, 3, and 4 nm for sample 1, 2, 3 and 4, respectively. However, the thickness of Zn0.97Mn0.03Se was fixed at 20nm. The Zn0.97Mn0.03Se/ZnSe0.8Te0.2 QW is a type-Ⅱ band alignment. Nevertheless, when the thickness of ZnSeTe was decreased to 1 nm, the type-Ⅰ emission come from ZnMnSe layer dominated the spectrum. Under applied electric field to 6KV/cm, the photoluminescence (PL) spectrum of sample 4 showed a strong red energy shift from 2.110 eV to 2.070eV However, the PL spectra of sample 1 and sample 2 did not change. It seems the electric field increases the chance of hole, which was confined in ZnSeTe layer, to transfer to ZnMnSe layer. Therefore, under applied electric field, the emission of Zn0.97Mn0.03Se/ZnSe0.8Te0.2 MQW changed from type-Ⅱ to type-Ⅰ.
並列關鍵字
無資料被引用紀錄
延伸閱讀
- Chen, W. C. (2016). Optoelectronic Devices Based on Earth Abundant Element (C, Cu, Zn, Sn, S, Se) by Solution and Vacuum Processes [doctoral dissertation, National Tsing Hua University]. Airiti Library. https://www.airitilibrary.com/Article/Detail?DocID=U0016-0411201614423467
- Hui, C. W. (2006). Positron annihilation spectroscopic studies of undoped n-type zinc oxide single crystal [master's thesis, The University of Hong Kong]. Airiti Library. https://www.airitilibrary.com/Article/Detail?DocID=U0029-1812201200014270
- Yoshimura, F., Ishizaki, M., Wakai, F., Hara, M., Odawara, O., & Wada, H. (2012). Optical Properties of Afterglow Nanoparticles Sr_2MgSi_2O_7: Eu^(2+), Dy^(3+) Capped with Polyethylene Glycol. Advances in Optical Technologies, 2012(), 373-378. https://doi.org/10.1155/2012/814745
- Cai, Y. L. (2002). Optical Properties of ZnTe/ZnSe1-xTex and ZnSe/Zn1-xMgxSySe1-y Multiple Quantum Well Grown by Molecular Beam Epitaxy [master's thesis, Chung Yuan Christian University]. Airiti Library. https://doi.org/10.6840/cycu200200101
- Huang, H. C. (2005). Molecular beam epitaxy and physical properties of modulation doped Zn0.86Cd0.14Se/ZnSe:Cl single quantum well [master's thesis, Chung Yuan Christian University]. Airiti Library. https://doi.org/10.6840/cycu200500302