單層與雙層聚氨酯直排輪輪子的製備及探討

The Preparation and Discussion of Solo and Stack Layer Polyurethane In-Line Skates Wheels

蘇榮基(Jung-Chi Su) ； 施文昌(Wen-Chang Shih)

《興大體育學刊》 14期 (2015/01) Pp. 15-25

摘要

本研究主要是以聚氨酯材料製備直排輪輪子並進行探討。研究結果如下：一、TDI系統有較高的抗拉強度及韌性，MDI系統有較高的密度，相同材質情形下，硬度高的材料有較高抗拉強度、密度及韌性。二、相同材質情形下，硬度高的輪子有較低的摩擦係數、較高的彈跳及較低的磨耗。三、TDI系統有較高的摩擦係數及較低的磨耗，抗疲勞測試輪子有脫膠；MDI系統有較高的的彈跳，抗疲勞測試輪子沒有脫膠。四、雙層輪子的彈跳優於單層輪子。

關鍵字

彈性體 ； 異氰酸酯 ； 多元醇

並列摘要

This study explores how Polyurethane was used as the raw material to manufacture the skate wheels. The results were as follows: 1. TDI system had a higher tensile strength and toughness; MDI system had a higher density; in the case of the same material, the high hardness of the material had higher tensile strength, density and toughness. 2. In the case of the same material, high hardness of wheels had a lower coefficiency of friction, higher rebound and lower abrasive. 3. TDI system had a high coefficiency, lower abrasive and anti-fatigue tested wheels that had glue off; MDI system had a high rebound, anti-fatigue tested wheels that had no glue off. 4. The rebound of stack layer wheels was better than that of solo layer wheels.

並列關鍵字

elastomer ； isocyanate ； polyol

參考文獻

山西省化工研究所 (2001)。聚胺酯彈性體手冊。中國山西省：化學工業出版社。

文慶珍、朱金華、姚樹人 (2002)。硬段結構對聚氨酯彈性體相容性及阻尼性能的影響。中國，高分子材料科學與工程，18(4)，117-120。

王曉鳴、劉鴻池、徐強 (2007)。基于 MDI/NDI 的聚氨酯彈性體的結構與性能。中國，合成橡膠工業，30(2)，107-110。

李明俊、王雲英、徐泳文、武化民 (2010)。聚氨酯材料阻尼改性方法與影響因素。中國，實驗技術與管理，27(7)，29-32。

李建勳 (2003)。優秀競速溜冰選手起跑動作之三度空間運動學分析 (未出版碩士論文)。國立屏東師院系體育學碩士班立體育學院，屏東縣。