Preparations of Indigo-dyed Sutra Paper for Receiving Gold-or Silver-paste Penned Scripture

本試驗研製之藍染金銀泥寫經紙，係以靛藍將纖維先行內添染色，再手工抄製而成，有別於傳統之成紙浸紙藍染法，此不僅可省卻繁複之多次浸染、洗滌發色工序，且可製得逐張色澤始末均－之高品質寫經紙。試驗研究之變因有漿料PH、添加順序、固色劑用量、媒染劑種類、低亞硫酸鈉（還原劑）、氫氧化鈉之用量、及接觸時間等。再選擇合適條件試製商業尺寸之藍染金銀泥寫經紙，此寫經紙不僅較市售一般寫經紙顏色深而沉穩，經UV照射後亦表現顏色的高度穩定性，遠非以一般造紙常用染料染色之對照組及市售寫經紙所可比擬。

• 期刊
• OpenAccess

含磷複合藥劑對造林木邊材耐雲芝菌腐朽性之增進效應

本研究應用2種有機磷藥劑（亞特松、亞培松）與2種醯氨類（本達樂、甲基多保淨）,l種烷基銨類（百克能）及3種磺胺藥劑（好立明、對氟苯磺胺、對氯苯磺胺）共配製12種不同組合之保存溶液，分別處理台灣杉、杉木及柳杉等造林木邊材。測定各項複合藥劑溶液在木材中之吸收量，並將部份處理材進行流失試驗。再依照室內促進試驗方法(CNS-6717)，觀測未經流失及經過流失2類試材對於雲芝菌之耐腐性能。以未經處理之素材為對照，探討藥劑處理對試材耐腐性之改良效應及流失性質對此效應之影響。試驗結果顯示，藥劑在木材中之吸收量主要分佈於1.8-4.5mg/cm^3之範圍。比較各試材對藥劑之吸收量，得知柳杉吸收力最強，其次為台灣杉，再次為杉木。藥劑處理材之耐腐性方面，相對於未處理之3種素材，均獲得有效改善。其中，不論經過或未經流失試驗，都以“亞特松與百克能”複合藥液之增進效應最為優良。其次，“亞培松與百克能”及“亞特松與對氟苯磺胺”2種藥劑組合對木材耐腐性均具有良好之增進效應。另外，“亞特松與甲基多保淨”複合藥劑也有良好之耐腐效應，唯經過流失處理後之耐腐效應則明顯下降。

• 期刊
• OpenAccess

防火劑加壓注入處理對合板抗燃性之影響

本試驗調配四組水溶性防火藥劑，以眞空加壓方式注入合板，期能製造符合國家標準CNS-6532規定之室內裝飾用耐燃合板。試驗結果得知防火劑注入處理之合板，其抗燃性以自行調配之FR防火劑者效果最好，其次為防火劑AF及Dricon；再次為Bi-fax。FR防火劑以20%重量百分率水溶液處理，合板厚度10mm以上者均可符合CNS-6532耐燃三級之要求，且其發熱量(tdθ)及發煙量(C(下標 A))亦較其他三組配方低，餘燄時間(tl)亦較短。防火劑AF抗燃效果，其著火性(tc)及發熱量均可達CNS-6532耐燃三級之要求，合板厚度12mm以上之餘燄時間未超過30sec，惟其發煙量偏高有待克服。而以Dricon防火劑處理之合板，其著火性、發熱量亦均可達CNS-6532耐燃三級之要求，惟其餘燄時間均超過30sec，故僅適合處理厚度15mm以上之合板。防火劑Bio-fax雖然具有低發煙量之特性，但因其自熄性（即餘燄時間）較差，故除了以20%濃度處理15mm厚之合板外，均無法符合CNS-6532耐燃三級之要求。至於合板處理前後之顏色變化，Dricon處理材變化最小，△E＊為2.21，其次為FR處理材，△E＊為3.84，而Bio-fax及AF處理材之顏色變化最大，△E＊分別為10.76及12.670。

• 期刊
• OpenAccess

塗裝與乙醯化處理對雲杉材音響特性之影響

近年來，由於良質之樂器用木材資源日益枯竭，為了保護樂器及改善其音響特性，塗裝或化學方法處理己普遍地被樂器製造業所應用。本試驗以北美產雲杉為試材，探討硝化纖維素塗裝、聚胺基甲酸酯塗裝及乙醯化處理對其音響特性之影響。試驗所獲之主要結果如下：雲衫之音響特性，當木理傾斜角為0°時，未塗裝材較塗裝材為佳，但隨木理傾斜角之增加，則塗裝材之動彈性係數略大於未塗裝材。因為木材之音響性質主要取決於順木理方向之特性，故塗裝會對音響性質產生不利之影響，實用上應儘量減少塗膜之厚度；又乙醯化處理使雲杉之動彈性係數略為下降，同時亦使內部摩擦降低，而音響變換效率之綜合指標K值，則隨此處理而略為上升。

• 期刊
• OpenAccess

扇平森林生態科學園遊憩滿意度分析－LISREL模型之應用

本研究應用LISREL模型來分析影響扇平森林生態科學園遊客遊憩滿意度的因子後，得知在影響遊客滿意度的因子中，是以「遊憩衝擊」這項變數對於遊憩滿意度的影響最大，而且是負面的影響，表示當遊客所感受的遊憩衝擊認知愈大時，其遊憩的滿意度會愈低。「環境設施」為影響遊憩滿意度的次大因素，表示當遊客所感受的環境設施認知愈佳時，其遊憩的滿意度會提高。相對於遊憩衝擊與環境設施的認知而言，「獨特性」與「解說服務」對遊客遊憩滿意度的影響並不大。未來在經營管理上應加強解說與推廣，以增進扇平科學園在環境生態教育上的功能。

• 期刊
• OpenAccess

廢棄木質粒片製造塑膠木料複合板之耐久性

本研究之目的為瞭解塑膠木料複合板之耐久性。試驗中於含木率50%之條件下，以無混鍊處理與混鍊處理製造兩種塑膠木料複合板。無混鍊複合板係將廢棄聚乙烯與木質粒片均勻混合後，於180℃進行熱壓而成。混鍊複合板係將廢棄聚乙烯與木質粒片以單螺桿擠押機進行混鍊處理後，切成小片進行熱壓而製成。耐久性之評估採用乾濕反覆處理，係將試片浸入60℃之熱水4h，再以60℃乾燥20h後，進行靜曲強度試驗。為了比較，亦使用尿素膠(UF)與三聚氰胺膠(MF)分別製造粒片板並進行同樣的乾濕反覆處理與靜曲強度試驗。由試驗結果得知，UF正粒片板與MF粒片板之靜曲強度隨著乾濕反覆週期數之增加明顯下降，同時UF粒片板之靜曲強度較MF粒片板者明顯降低。經16週期處理後，MF粒片板仍顯示出具有相當程度之耐久性能。無混鍊複合板與混鍊複合板經2週期以上之乾濕反覆處理後，其靜曲強度均較MF粒片板者大，在乾濕處理4週期時，無混鍊複合板之靜曲強度明顯降低，在4週期以後其降低之程度趨於緩和，在各週期之靜曲強度中，混鍊複合板者較無混鍊複合板者明顯增大。

• 期刊
• OpenAccess

台灣油杉空粒種子形成原因的探討

Cone and seed development was observed from 1993 to 1998 in wind-pollinated Keteleeria davidlana (Franchet) Beissner var. formosana Hayata trees grown at Taipei Botanical Garden. Seed efficiencies per cone (percent filled seed per cone divided by seed potential) were persistently less than 1% during the investigation period. Sections of large seeds at different stages during the period from polyembryos to cotyledonary embryos revealed that 80% of them were successfully fertilized initially, and then almost all degenerated before developing into mature embryos. Cone length growth was evidently affected by the number of large seeds inside the cone, and there was a very significant (p＜0.001) linear regression between these 2 factors. Before fertilization occurred, conelets and ovules reached the same sizes as did mature cones and seeds. Pollen grains had a high germination percentage and were found in mycropyles of ovules, indicating no pollination barrier between catkins and conelets. Unpollinated cones containing small seeds were not shed. All these facts indicate that ovules grew after they obtained pollen, subsequently stimulating cone development. The great variations of large seeds, numbering from 50 to 114 per cone, and cone length, differing from 6.7 to 9.0 cm, in 6 years came from the pollination degree of ovules. According to the year with the best large-seed production, the reasons for empty seeds could be estimated as follows: Seed potential per cone calculated as 2 times the number of fertile ovuliferous scales was about 206 seeds. Percentages of seed losses resulting from pre-and post-pollination ovule abortion, prezygotic factors, embryo degeneration, and efficient seed were 33%, 27%, 39%, and＜1%, respectively. Even in the year with good pollination effectiveness, embryo degeneration was so great as to cause most fertilized seeds to become empty.

• 期刊
• OpenAccess

紅檜與台灣扁柏低的葉綠體DNA遺傳變異及族群分化

本文以PCR/RFLP及核苷酸序列分析紅檜與台灣扁柏之葉綠體基因組之多型性。結果發現紅檜與台灣扁柏於棲蘭山與阿里山兩族群間，在兩個葉綠體DNA之基因間區間序列其限制酶片段長度及核苷酸序列均沒有差異。如此低的遺傳變異可能是因為現今之紅檜與台灣扁柏族群為冰河期存在之大族群的殘留小族群，而未必是花粉散播所提供之基因交流極為頻繁所造成。trnV-trnM基因間區間序列在紅檜與台灣扁柏兩者間有兩個HinfI之酶切點之差異，在PetG-trnP基因間區間序列也發現台灣扁柏與紅檜之間有限制酶片段長度及其他點突變。紅檜與台灣扁柏間之親源關係，仍有待與其它扁柏屬植物，特別是日本扁柏比較後才能明確瞭解。

• 期刊
• OpenAccess

藤枝地區台灣杉人工林疏伐修枝效果之研究

本研究探討台灣衫疏伐及修枝之效應，以期提高木材質量生長。供試林分為屏東林區管理處荖濃事業區第73林班，本所原實施疏伐修枝試驗之26年生台灣杉人工林，繼續施行第二次疏伐及第三次修枝試驗。疏伐方式計分為每公頃保留600株；800株：1000株及未疏伐之對照區。修枝處理則分為修枝6m樹高：修枝8m樹高及未修枝之對照區。經處理6年後之研究結果顯示，第二次疏伐以每公頃保留600株和800株之處理效應較佳，可增進胸徑、樹高、胸高斷面積和材積之生長。而樹冠幅係隨疏伐強度之增大而增大，枝下高則隨疏伐強度之增大而減小。第三次修枝對林分生長無明顯差異，即使修枝至8m樹高亦然，修枝6年後傷口完全癒合者達95%，修枝確有助無節材之生產。

• 期刊
• OpenAccess

六龜試驗林森林經營決策中發展地方民眾參與之研究

本研究旨在探討六龜和茂林居民與森林經營者之互動關係，以評估當地民眾參與森林經營的可行性。本研究採用史料和文獻調查、政府次級統計資料蒐集、與田野調查等方法。蒐集與調查之資訊包含：當地人口與產業結構、區位特性、土地利用變遷歷程、居民對森林議題的意見等四類。民眾意見係透過現場訪談蒐集，包括以下五項與當地森林相關之議題：禁漁政策、山地保留地設置、還我土地運動、風景特定區開發案，以及河岸強制造林等五項。研究結果顯示，茂林鄉較密結的社會結構使其比六龜鄉更有利於集體行動的形成，而從民眾意見的分析顯示出多納社區已具備民眾參與的能力。本研究建議，森林經營需納入民眾參與的機制，可改善決策的偏差，並保障能達到社會公平的經營目標。