Fracture Load of fiber-reinforced Repaired Acrylic Resin Provisional Fixed Partial Denture

吳育琦(Yu-Chi Wu) ； 王震乾(Jen-Chyan Wang) ； 羅秋萍(Cho-Ping Rong) ； 洪純正(Chun-Cheng Hung)

《Taiwan Journal of Oral Medicine & Health Sciences》 21卷2期 (2005/10) Pp. 75-84

https://doi.org/10.7059/TJOMHS.200510.0075

摘要

The purpose of this study was to evaluate the fracture load and fracture pattern of repaired acrylic resin provisional restoration, which had been reinforced with various fibers. It also aimed to investigate the relationships between type/surface treatment of fibers and fracture pattern/fracture strength of samples. In the experiment, first, 60 standardized 4-unit bridge samples n=60 over mandibular posterior region were fabricated with PMMA resin. Next, they were divided into 6 groups evenly. Besides 10 intact samples as control group, other 50 samples were repaired with resin or glass fiber with or without light curing/polyethylene fibers (with or without silane treatment). The fracture load of samples were tested with an universal testing machine and fracture pattern of all specimens were recorded. The fracture surfaces of selective samples were observed under SEM. All data were statistically analyzed using one-way ANOVA and Tukey's pairwise comparison test. The results indicated the fracture load of glass/polyethylene fiber-reinforced groups were statistically significant higher than acrylic resin repaired group (P＜0.05). However, there is no statistical difference between fiber-reinforced groups and intact sample groups. As for fracture pattern, most of all samples are display ”partial” fracture. The results of present study showed acrylic resin FPD reinforced with glass or polyethylene fibers do exhibit higher fracture loads as compared to samples without reinforcement. The way of surface treatment to fibers seems to be a dominate factor influence the fracture load of a long-span repaired provisional FPD.

關鍵字

纖維 ； 壓克力樹脂 ； 修補

並列摘要

The purpose of this study was to evaluate the fracture load and fracture pattern of repaired acrylic resin provisional restoration, which had been reinforced with various fibers. It also aimed to investigate the relationships between type/surface treatment of fibers and fracture pattern/fracture strength of samples. In the experiment, first, 60 standardized 4-unit bridge samples n=60 over mandibular posterior region were fabricated with PMMA resin. Next, they were divided into 6 groups evenly. Besides 10 intact samples as control group, other 50 samples were repaired with resin or glass fiber with or without light curing/polyethylene fibers (with or without silane treatment). The fracture load of samples were tested with an universal testing machine and fracture pattern of all specimens were recorded. The fracture surfaces of selective samples were observed under SEM. All data were statistically analyzed using one-way ANOVA and Tukey's pairwise comparison test. The results indicated the fracture load of glass/polyethylene fiber-reinforced groups were statistically significant higher than acrylic resin repaired group (P＜0.05). However, there is no statistical difference between fiber-reinforced groups and intact sample groups. As for fracture pattern, most of all samples are display ”partial” fracture. The results of present study showed acrylic resin FPD reinforced with glass or polyethylene fibers do exhibit higher fracture loads as compared to samples without reinforcement. The way of surface treatment to fibers seems to be a dominate factor influence the fracture load of a long-span repaired provisional FPD.

並列關鍵字

fiber ； acrylic resin ； repair