磷酸化鈦鋯氧化物表面特性分析與對NH4+離子吸附行為探討

Surface Characterization of Phosphated Zirconia-Titania and Its Adsorption Behavior for Ammonium Ions

李美華(Mei-Hua Li)

指導教授 ： 張淑閔

國立交通大學/工學院/工學院永續環境科技學程/碩士(2015年)

https://doi.org/10.6842/NCTU.2015.00852

摘要

本研究以離子液體輔助水熱法合成之磷酸化鈦鋯氧化物固體酸作為NH4+離子吸附劑，並對其表面特性進行分析以探討其對NH4+離子吸附行為的影響；透過一系列批次實驗進行探討等溫和動力吸附模式，其操作參數包括:不同吸附劑量、pH值和溫度對NH4+離子吸附能力的影響。研究結果發現，磷酸化鈦鋯氧化物團聚形成粒徑大小為400~500nm，比表面積為247±20m2/g，陽離子交換容量(cation exchange capacity , CEC )約為250±20meq/g，零電位點（pH of zero point charge , pHzpc）介於3.3±0.2，而分散於水溶液中可使溶液pH值降至4.4±0.5，表示磷酸化鈦鋯氧化物具有酸性及陽離子交換能力；動力吸附平衡時間為30min，符合擬二階動力模式；磷酸化鈦鋯氧化物對於NH4+吸附行為較符合Freundlich吸附模式且為自發性放熱反應，H0= -5.76kJ/mole，最佳吸附劑量為70g/L，不同pH環境下吸附量隨著pH值增加而增加至pH值為6.25；在固態酸鹼吸附劑上，對於銨離子去除條件為靜電引力吸附及離子交換。

關鍵字

固態酸 ； 吸附 ； 銨離子 ； 陽離子交換容量 ； 零電位點pH值

並列摘要

This study investigated the surface properties and NH4+ adsorption characteristics of the phosphated titanium-zirconium oxide solid acid prepared by an ionic-liquid assisted hydrothermal method. In addition, the correlation between the adsorption capability and the surface properties of the adsorbent was elucidated. Adsorption isotherm and kinetic study were carried out from a series of batch tests. Moreover, the influences including adsorbent dosage, pH values, and temperatures on the adsorption capability were examined. The results showed that the aggregated particles had a size ranged between 400-500 nm with the specific surface area of 247±20m2/g. The cation exchange capacity (CEC) was 250±20meq/100g, and the pH at zero-point-of-charge (pHzpc) was 3.3±0.2. Dispersion of the adsorbent in water decreased the pH to 4.4±0.5, indicating acidity and cationic exchanging ability of the phosphated titanium-zirconium oxide. The adsorption equilibrium time was 30 minutes and the adsorption kinetic data can be well fitted by a pseudo-second-order model. The Freundlich model fits the adsorption isotherm and the adsorption was an exothermic process with H0= -5.76 kJ/mol. The optimal adsorbent dosage was 70g/L, and the adsorption amount increased with the pH values till pH= 6.25. These results reveal that the ammonia ions are removed in terms of electrostatic attraction and cation ion exchange on the solid-acid-based adsorbent.

並列關鍵字

Solid acid ； Adsorption ； Ammonia ions ； Cation exchange capacity ； pH of zero potential point

參考文獻

13.Samantaray, Santosh Kumar, and Kulamani Parida. "Studies on anion-promoted titania: 3. Effect of concentration and source of phosphate ion, method of preparation, and activation temperature on redox, acid–base, textural and catalytic properties of titania." Journal of Molecular Catalysis A: Chemical 176.1 (2001): 151-163.

52.Makeswari, M., and T. Santhi. "Removal of malachite green dye from aqueous solutions onto microwave assisted zinc chloride chemical activated epicarp of Ricinus communis." (2013).

81.沈柏汎,Effects of tungatate and phosphate species on the acidity of ZrO2-TiO2 soild acids,(2015).

1.Wang, Shaobin, and Yuelian Peng. "Natural zeolites as effective adsorbents in water and wastewater treatment." Chemical Engineering Journal 156.1 (2010): 11-24.

2.Wang, Yifei, Feng Lin, and Wenqin Pang. "Ion exchange of ammonium in natural and synthesized zeolites." Journal of hazardous materials 160.2 (2008): 371-375.