運用分子動力學方法模擬橢球型鉑奈米粉末在金屬3D列印製程中，分析橢球型鉑奈米粉末在室溫環境下與雷射燒結製程過程之中的情況，分析其熱機特性，並找出最佳的製程參數。在室溫環境之下，橢球型鉑奈米粉末會自體燒結，均方根位移會隨著加熱速率和製程溫度的升高而上昇，加熱速率越慢，鉑原子的擴散越均勻。鉑奈米粉末之聚結溫度為841K-1435K，熔化溫度為1138K-1485K，皆比巨觀尺度鉑的熔化溫度2041.4K低很多。本文運用國研院國網路中心的超級電腦（台灣杉一號，16核心）運算速度，比起家用筆記型電腦平均快了三倍以上。
關鍵字
無資料參考文獻
ASTM International, F2792: Standard terminology for additive manufacturing technologies, (2013)
H. Lipson and M. Kurman, Fabricated. The new world of 3D printing, Wiley, Indianapolis, IN, (2013).
W. E. Frazier, Metal additive manufacturing: a review, Journal of Materials Engineering and Performance. Vol. 23, pp. 1917-1928, (2014).
B. P. Conner, G.P. Manogharan, A.N. Martof, L.M. Rodomsky, C. M. Rodomsky, D.C. Jordan and J.W. Limperos, Making sense of 3-Dprinting: Creating a map of additive manufacturing products and services, Additive Manufacturing. Vol.1, pp. 64-76, (2014).
M. Vaezi, H. Seitz and A. Yang, A review on 3D micro-additive manufacturing technologies, The International Journal of Advanced Manufacturing Technology. Vol. 67, p.p. 1721-1754, (2013).
延伸閱讀
- 江右君、吳帛軒、岳恆屹、林俊宇、楊景松（2021）。以官能基化奈米碳管作為奈米鉑觸媒之載體的特性研究。燃燒季刊，(114)，9-23。https://doi.org/10.30041/CQ.202108_(114).0002
- 黃啟華（2005）。奈米觸媒顆粒成長之奈米碳管應用於場效電晶體之研究〔碩士論文，國立臺灣大學〕。華藝線上圖書館。https://doi.org/10.6342/NTU.2005.01447
- 翁永春（2005）。氣輔軟模紫外光固化微奈米壓印製程應用於製作光波導元件之研究〔碩士論文，國立臺灣大學〕。華藝線上圖書館。https://doi.org/10.6342/NTU.2005.10077
- 賴思妤（2014）。碳奈米複合材料與Eucalyptus globulus生物合成奈米銀粒子之應用〔碩士論文，國立臺北科技大學〕。華藝線上圖書館。https://doi.org/10.6841/NTUT.2014.00042
- Liu, S. Y. (2008). 利用對流性自組形成之奈米球微影術製作週期性圖案化藍寶石基板 [master's thesis, National Taiwan University]. Airiti Library. https://doi.org/10.6342/NTU.2008.01890