Kinetic Analysis of the Hydrogen Oxidation Reaction at Nafion Film Covered Pt-black Rotating Disk Electrodes

The kinetics of the H2 oxidation reaction at Nation film covered Pt-black rotating disk electrodes (RDEs) in 0.5 M H2SO4 at 298 K was investigated by varying the Pt loading, Nation film thickness, and rotating rate. The equation describing the H2 oxidation kinetics at an RDE with a Nafion film covered porous Pt layer was derived, assuming a Tafel-Volmer mechanism and taking into account the mass transfer resistances in the aqueous electrolyte, Nafion film. and Pt layer. The H2 oxidation reaction at the Pt layer was proved to be reversible and the measurable current density was determined entirely by the mass transfer of H2 in the aqueous electrolyte and the Nafion film; the apparent kinetic current density measured was due to die experimental error. More accurate results of kinetic analysis were obtained in this work than our results reported previously.

並列關鍵字

Pt-black ； Nafion ； Hydrogen oxidation ； Rotating disk electrode ； Fuel cell

國際替代計量

未授權

主題瀏覽