Polymerization Kinetics for the Preparation of Poly (p-divinylbenzene)

The polymerization kinetics for the preparation of poly (p-divinylbenzene (p-DVB)) via a miniemulsion polymerization process was studied by the gravimetric analysis and the transmission electron microscopy (TEM) analysis. The influence of the variation of both initiator concentration and polymerization temperature on the polymerization rate was investigated and also the activation energy of p-divinylbenzene was estimated. The evolution of polymer particles was observed by the electronmicrographs and the relatively large size of polymer particles without the formation of coagulum was obtained in the miniemulsion polymerization process.

並列關鍵字

p-Divinylbenzene ； Miniemulsion ； Polymerization ； Kinetics

被引用紀錄

Chen, J. R. (2010). 氧化鉺薄膜於電阻式記憶體的製作與轉態特性之研究 [master's thesis, National Chiao Tung University]. Airiti Library. https://doi.org/10.6842/NCTU.2010.00421

Tsai, C. H. (2009). 鈦上電極對濺鍍法製備之氧化鋯薄膜於電阻式轉換記憶元件之研究 [master's thesis, National Chiao Tung University]. Airiti Library. https://doi.org/10.6842/NCTU.2009.00696

Chang, Y. F. (2009). 氧空缺與相變化在氮化鈦/二氧化矽/鐵白金結構電阻式非揮發性隨機存取記憶體的影響 [master's thesis, National Chiao Tung University]. Airiti Library. https://doi.org/10.6842/NCTU.2009.00431

王思琁（2011）。提升ZigBee定位系統準確性之定位信號估算及參考節點選擇法之研究〔碩士論文，國立虎尾科技大學〕。華藝線上圖書館。https://doi.org/10.6827/NFU.2011.00018

許峰誠（2011）。以射頻濺鍍製作異質接面矽太陽能電池之研究〔碩士論文，國立中央大學〕。華藝線上圖書館。https://www.airitilibrary.com/Article/Detail?DocID=U0031-1903201314425056

國際替代計量

Polymerization Kinetics for the Preparation of Poly (p-divinylbenzene)

未授權

主題瀏覽