A Method of Growing YBa2Cu3Oy, Thin Films on Mismatched Substrates
並列摘要
We have studied YBa2Cu3Oy bi-layer thin films deposited at two different temperatures on mismatched substrates, such as MgO (a=b=c=0.412nm) and YSZ (a=b=c=0.5139nm). The bottom layer is deposited at a lower temperature (660 C) while the top layer is deposited at the usual temperature (750 ''C). The Tc of the bilayer film is significantly higher than that of the single layer for YSZ substrates. The five-circle X-ray results show different in-plane orientations for these two bi-layer thin films on MgO and YSZ substrates. The results are also compared with bi-layer thin films grown on well-matched substrates, such as SrTiO3 (a=b=c=0.3905nm).
並列關鍵字
無資料被引用紀錄
林永杰（2010）。碳紙上生長奈米碳管及其在甲醇燃料電池上之應用〔碩士論文，國立清華大學〕。華藝線上圖書館。https://doi.org/10.6843/NTHU.2010.00204
蘇文碩（2002）。躁鬱症患者的人格特質與其自我照顧能力，生活適應關係之研究 ─ 以中山醫學大學附設醫院樣本為例〔碩士論文，中原大學〕。華藝線上圖書館。https://doi.org/10.6840/cycu200200263
延伸閱讀
- 蘇志翔（2011）。YBa2Cu3O7-δ thin film prepared by femtosecond pulsed laser deposition〔碩士論文，國立交通大學〕。華藝線上圖書館。https://doi.org/10.6842/NCTU.2011.00671
- Chui, T. C. (1998). Growth and characteristization of YBa2Cu3Ox thin and ultrathin films [master's thesis, The University of Hong Kong]. Airiti Library. https://www.airitilibrary.com/Article/Detail?DocID=U0029-1812201200006055
- Gan, F. Y., Chu, M. L., Chang, H. L., Wang, C., Jiang, C., Wu, K. H., Gou, Y. S., & Uen, T. M. (1990). In-Situ Growth of Y-Ba-Cu-0 High-Tc Superconducting Thin Films by Pulsed Laser Deposition Method. Chinese Journal of Physics, 28(4), 367-372. https://www.airitilibrary.com/Article/Detail?DocID=05779073-199008-201302220022-201302220022-367-372
- Hsu, S. N., & Lin, R. J. (1993). Microstructural Study of YBa2Cu3O7-χ Thin Films on Si with MgO as a Buffer Layer. Chinese Journal of Physics, 31(6S), 1239-1244. https://www.airitilibrary.com/Article/Detail?DocID=05779073-199312-201212270032-201212270032-1239-1244
- 張耀文、劉祐承、邱濬謙、吳秉駿、楊展其（2021）。Fabrication of Freestanding Single-Crystalline Oxide Thin Films Using YBa_2Cu_3O_(7-x) as a Sacrificial Layer。真空科技，34(1)，5-12。https://www.airitilibrary.com/Article/Detail?DocID=1017091x-202103-202104200011-202104200011-5-12