並列摘要
MBE-grown highly strain multiple quantum wells of InGaAs(Sb) and InGaAsN(Sb) were investigated by room temperature photoluminescence(RT-PL) and high resolution x-ray diffraction(HRXRD). By adding dilute Sb on the highly strained InGaAs and InGaAsN MQWs, the RT-PL spectra exhibits significantly increased intensity and narrowed line-width. The X-Ray c4ffraction curve was obtained the better flat interface and less strain between QW and barrier layer. Studies reveal the role of Sb as surfactant in the growth of quaternary and quinary alloy.
並列關鍵字
無資料延伸閱讀
- Chen, P. H. (2006). Study of the Hydrogen Effect on Si-SiO2 Interface Property for MOS Capacitor after Water Immersion [master's thesis, National Taiwan University]. Airiti Library. https://doi.org/10.6342/NTU.2006.03110
- Lin, G. J. (2011). Photovoltaic Physics of InGaN/GaN Multiple Quantum Wells [master's thesis, National Taiwan University]. Airiti Library. https://doi.org/10.6342/NTU.2011.00625
- Lin, Y. L. (2006). Optical Studies on Pre-strained InGaN/GaN Quantum Wells [master's thesis, National Taiwan University]. Airiti Library. https://doi.org/10.6342/NTU.2006.01175
- Lee, C. H., Chang, Y. H., Lin, H. H., & Lee, C. P. (1998). Formation of D^- Centers in GaAs/AlGaAs Quantum Wells. Chinese Journal of Physics, 36(3), 519-526. https://www.airitilibrary.com/Article/Detail?DocID=05779073-199806-201211050037-201211050037-519-526
- 陳右諭（2000）。Photoreflectance Research of GaAs/GaNAs Quantum Wells Structure〔碩士論文，國立臺灣師範大學〕。華藝線上圖書館。https://www.airitilibrary.com/Article/Detail?DocID=U0021-2603200719104989