使用非真空塗佈法製備銅銦硒薄膜太陽能電池特性研究

The Study of Fabricate CuInSe2 Thin Film Solar Cell by Using Non-Vacuum Coating Process

王彥超(Yen-Chao Wang) ； 劉旺林(Wang-Lin Liu) ； 許朝凱(Chao-Kai Hsu) ； 吳淑媛(Shu-Yuan Wu) ； 朱筱鈞(Siau-Jyun Jhu)

《科儀新知》 173期 (2009/12) Pp. 28-34

https://doi.org/10.29662/IT.200912.0003

摘要

本研究利用溶劑熱法製備銅銦硒(CIS)奈米粉體，後以塗佈方式將CIS漿料塗佈於鈉玻璃基板上形成前驅層，再置於高溫管狀爐管中進行燒結製程，使之形成具有黃銅礦結構特性薄膜，改變製程參數調整材料本身的粒徑大小和結晶性。由本實驗之結果得到，熱處理溫度500℃、持溫10分鐘，即可得到具有黃銅礦結構特性之CuInSe2薄膜。

並列摘要

In this research, we used the solvothermal method to synthesize CuInSe2 nano powder. Then deposit thin layers of CuInSe2 inks on sodium glass substrates using simple non-vacuum techniques. Chalcopyrite-type thin film CuInSe2 was successfully prepared by using thermal processing. We had demonstrated it that by controlling and changing the thermal processing temperature, reaction time to control the particle size and crystal phase. We receive a result that thermal treatment of 500℃/10 min is the best parameter under environment.