High Rate Anodic Dissolution of Stainless Steel 316 (SS316) Using Nano Zero Valent Iron as Reducing Agent
並列摘要
The experiments on electrochemical machining of stainless steel SS316 have been carried out according to designed experimental plan to observe the effect of nano zero valent iron (NZVI) mixed electrolyte solution on material removal rate. Dependence of material removal rate on feed rate in presence of NZVI has been determined and compared with theoretical values. These comparative investigations for MRR are given in tabular format with graphical representation. The significant effect on MRR was observed; when NZVI mixed aqueous NaCl solution was used as an electrolyte due to its high reducing characteristics. The observed experimental results were found to be quite close with theoretical results.
被引用紀錄
吳俊逸（2016）。多功能性有機無機複合顆粒之製備與反應機制研究〔博士論文，中原大學〕。華藝線上圖書館。https://doi.org/10.6840/cycu201600009
Wang, S. L. (2015). 頻率選擇性衰減通道下之合作式與感知通訊研究 [doctoral dissertation, Chung Yuan Christian University]. Airiti Library. https://doi.org/10.6840/CYCU.2015.00409
方立陞（2011）。三元 Ti-5Cr-xMo 合金於牙科應用之研究〔碩士論文，中臺科技大學〕。華藝線上圖書館。https://doi.org/10.6822/CTUST.2011.00047
Liu, C. Y. (2015). 前瞻性材料的機械性質—以熱電材料與金屬玻璃為例 [master's thesis, National Taiwan University]. Airiti Library. https://doi.org/10.6342/NTU.2015.02313
Hsu, Y. F. (2012). 石墨烯新穎電子傳輸性質之理論研究 [doctoral dissertation, National Taiwan University]. Airiti Library. https://doi.org/10.6342/NTU.2012.01087
延伸閱讀
- 黃國政（2007）。The Chemical Synthesis and Application of Nanosized Metallic Materials (Nickel, Iron and Silver)〔博士論文，國立清華大學〕。華藝線上圖書館。https://doi.org/10.6843/NTHU.2007.00051
- Wang, Z. M., Demessie, E. S., & Hassan, A. A. (2011). Selective Oxidation Using Flame Aerosol Synthesized Iron and Vanadium-Doped Nano-TiO_2. Journal of Nanotechnology, 2011(), 80-90. https://doi.org/10.1155/2011/209150
- 李佳旻（2019）。Removal of Arsenic by Iron/Manganese-doped Titanium Dioxide Nanotubes〔碩士論文，國立臺灣大學〕。華藝線上圖書館。https://doi.org/10.6342/NTU201904162
- 鄭維仁、陳丁誌、朱慶霖、溫仕寶、王朝正（2014）。Hot Corrosion of Cr-Mo Steel in Molten LiNO_3-NaNO_3-KNO_3 Eutectic Salt。防蝕工程，28(2)，55-63。https://doi.org/10.6376/JCCE.201406_28(2).0001
- 張錦泉、柏宏基、林義宗（1993）。Electrochemical Behavior of Zinc Sacrificial Anode in 3.5wt% NaCl Solution。防蝕工程，7(4)，34-38。https://doi.org/10.6376/JCCE.199312.0034