Subwavelength Silicon-Wire Photonics

次波長矽線波導光學

邱威超(Wei-Chao Chiu)

指導教授 ： 李明昌

國立清華大學/電機資訊學院/光電工程研究所/博士(2011年)

https://doi.org/10.6843/NTHU.2011.00642

摘要

A new technology using hydrogen annealing and thermal oxidation is introduced to make subwavelength photonic wires as well as to achieve three-dimensional photonic integration on a silicon-on-insulator (SOI) substrate.
Due to the hydrogen-annealing-induced profile transformation, the silicon wire with very smooth sidewall is accomplished, showing the propagation loss as low as 1.26 dB/cm. Moreover, a tapered beam spot-size converter is developed and monolithically integrated with subwavelength silicon wires. Owing to the low on-chip optical loss, nonlinear optical processes such as four-wave mixing, Raman emission and amplification, and anti-Stokes Raman conversion are observed at the pump power around just tens of milliwatts.
To achieve large-scale integration of photonic circuits, waveguide couplers are essential to device integration and functioning. Thus a very compact two-dimensional multimode interference coupler with dual-layer silicon photonic wires is demonstrated for the first time using the similar fabrication technology. Two devices, a 1×1 cross power coupler and a 1×4 power splitter, are presented and characterized. The experimental result shows a 1.1-nm 3-dB transmission bandwidth, and on-chip coupling losses of 8.6 dB and 2.84 dB with respect to the 1×1 cross coupler and 1×4 splitter. This work shows the possibility to realize photonic integrated circuits in three dimensions on a silicon-on-insulator (SOI) substrate.
For realizing active functions such as optical switch, signal modulation and attenuation on photonic circuits via the interference-type devices, it is important to control optical phase without amplitude dependency. However, it is challenging to be accomplished by using the conventional p-i-n or pn phase modulators based on the plasma dispersion effect due to the strong free-carrier absorption. A deformable silicon wire actuated by micro-electro-mechanical-systems (MEMS) offers an efficient way to control optical phase without causing much amplitude variation. By mechanically stretching the waveguide physical length, a 0.1-pi phase shift could be achieved via actuation of a single actuator at 240 V. The amplitude variation during the mechanical actuation is measured to be within 0.063 dB for both TE- and TM-polarized waves. To the authors’ best knowledge, this is the first time that a waveguide phase modulator decoupling from amplitude variation has been realized based on MEMS and silicon photonic technologies.

關鍵字

hydrogen annealing ； integrated optics ； multimode inteference ； micro-electro-mechanical systems ； silicon photonics ； silicon-on-insulator

參考文獻

[2] R. Dekker, N. Usechak, M. Forst, and A. Driessen, "Ultrafast nonlinear all-optical processes in silicon-on-insulator waveguides," Journal of Physics D-Applied Physics, vol. 40, pp. R249-R271, Jul 2007.

[3] L. M. Tong, R. R. Gattass, J. B. Ashcom, S. L. He, J. Y. Lou, M. Y. Shen, I. Maxwell, and E. Mazur, "Subwavelength-diameter silica wires for low-loss optical wave guiding," Nature, vol. 426, pp. 816-819, Dec 2003.

[4] S. G. Leon-Saval, T. A. Birks, W. J. Wadsworth, P. S. J. Russell, and M. W. Mason, "Supercontinuum generation in submicron fibre waveguides," Optics Express, vol. 12, pp. 2864-2869, Jun 2004.

[6] Y. Vlasov and S. McNab, "Losses in single-mode silicon-on-insulator strip waveguides and bends," Opt. Express, vol. 12, pp. 1622-1631, 2004.

[7] T. Tsuchizawa, K. Yamada, H. Fukuda, T. Watanabe, J. Takahashi, M. Takahashi, T. Shoji, E. Tamechika, S. Itabashi, and H. Morita, "Microphotonics devices based on silicon microfabrication technology," IEEE Journal of Selected Topics in Quantum Electronics, vol. 11, pp. 232-240, Jan-Feb 2005.