脈衝雷射沉積法製備釔銩鐵石榴石薄膜的探討：結構、光學與磁性研究

Structural,Optical and Magnetic properties of Tm-doped YIG thin films grown by pulsed-laser deposition

林建良(Lin Jian-Liang)

指導教授 ： 駱芳鈺

國立臺灣師範大學/理學院/物理學系/碩士(2018年)

https://doi.org/10.6345/THE.NTNU.DP.019.2018.B04

摘要

本論文以脈衝雷射蒸鍍法在c方向單晶藍寶石基板上製備100nm厚的TmxY3-xFe5O12薄膜，並探討薄膜鍍膜速率、薄膜的結構特性、光學性質及磁性的關係，其中單位面積雷射能量為3.5 J/cm2，鍍膜氧壓分別為3×10-1 mbar，Tm取代比例為x=0~3，基板溫度為750℃。
TmxY3-xFe5O12薄膜鍍膜速率不隨著取代比例增加而加快，鍍膜速率並無特定趨勢。X光繞射及拉曼散射光譜顯示隨著取代比例增加，薄膜由多晶轉為非晶結構，代表基板與薄膜的晶格失配度過大而無法形成單晶結構，薄膜在x=1.5時結晶品質最好。X光電子能譜分析，取得薄膜的銩與釔的實驗比例與理論值不符。利用原子力顯微鏡來看表面形貌與粗糙度，表面有許多柱狀晶體與粗糙度大約為20nm粗糙表面。超導量子干涉磁量儀測定與柯爾磁光顯微鏡結果顯示所有薄膜都沒有表現出磁性。

關鍵字

釔鐵石榴石 ； 銩 ； 脈衝雷射鍍膜

並列摘要

In this paper, a 100nm thick TmxY3-xFe5O12 film was prepared on a c-oriented single crystal sapphire substrate by pulsed-laser deposition. The relationship between the film coating rate, the structural properties, optical properties and magnetic properties of the film was investigated. The laser energy fluence is 3.5 J/cm2, the coating oxygen pressure was 3×10-1 mbar, the Tm substitution ratio was x=0~3, and the substrate temperature was 750 °C.
The coating rate of TmxY3-xFe5O12 film does not increase with the increase of the substitution ratio, and there is no specific trend of coating rate. X-ray diffraction and Raman scattering spectroscopy show that the structure of thin films changes from polycrystalline to amorphous as Tm concerntration increases,and the film has the best crystal quality at x=1.5. According to the x-ray photoelectron spectroscopy, the experimental ratio of thulium to yttrium of the film is not in agreement with the theoretical value. The surface topography and roughness were observed by atomic force microscopy with a number of columnar crystals and a rough surface of approximately 20 nm roughness. The results of SQIUID and Kerr Magneto-Optical Microscopy showed that all films showed no magnetic properties.

並列關鍵字

Yttrium iron garnet ； Thulium ； Pulsed-laser deposition (PLD)

參考文獻

1. 余威廷，2005，添加高分子螯合劑對生成釔鐵氧化物結構之影響研究(碩士論文)。南台科技大學。

2. Murata Mfg. Co., Ltd., 2-26-10 Tenjin, Nagaokakyo, Kyoto 617-8555, Japan

3. Deltronic Crystal Isowave - Yttrium Iron Garnet - 2013-02-14

4. Makiyyu AbdullahiMusa,Raba'ah SyahidahAzis,Nurul HudaOsman,JumiahHassan,TasiuZangina，2017，Structural and magnetic properties of yttrium iron garnet (YIG) and yttrium aluminum iron garnet (YAlG) nanoferrite via sol-gel synthesis，Result in Physics Volume 7 Pages1135-1142

5. 蔡昌彥，2017，石榴石鐵氣體之磁性與光學特性之分析(碩士論文)，國立屏東大學。