二維材料二硫化鈮表面結構與電性初探

Preliminary study on surface structure and electrical properties of two-dimensional material niobium disulfide

黃祺翔(Huang Chi-Hsiang)

指導教授 ： 傅祖怡

國立臺灣師範大學/理學院/物理學系/碩士(2022年)

https://doi.org/10.6345/NTNU202201099

摘要

二硫化鈮是屬於金屬性二維材料中的過度金屬二硫族化物，雖然理論學家已經對於二硫化鈮有許多報導，但在奈米級的表面相關影像卻非常少，可能源自於對二硫化鈮表面掃描時要取得清晰的影像並不容易，需要有相當的掃描經驗與對掃描影像的後續處理才能取得較清晰的二硫化鈮奈米級表面。
本篇實驗透過掃描穿隧式電子顯微鏡觀察二硫化鈮機械剝離前後與曝氧5到40分鐘的表面缺陷並分析以及使用掃描穿隧能譜功能量測其不同狀態下的電性變化。觀察到隨著曝氧時間增長二硫化鈮表面上的暗點和亮點缺陷有變大的趨勢，至於在費米能階附近的電阻會隨著與氣體接觸而上升，而正負偏壓下會逐漸回到如機械剝離前的狀態。

關鍵字

掃描穿隧式電子顯微鏡 ； 掃描穿隧能譜 ； 二硫化鈮 ； 機械剝離 ； 曝氧實驗

並列摘要

Niobium disulfide is a transition metal dichalcogenide (TMDs) in metallic two-dimensional materials. Although theorists have reported many reports on niobium disulfide, there are very few on nanoscale surface images. Since it is not easy to obtain a clear image when scanning the surface of niobium disulfide, considerable scanning experience and subsequent processing of the scanned image are required to obtain a clearer nanoscale surface of niobium disulfide.
In this experiment, the surface defects on NbS2 before and after mechanical exfoliation and exposure to oxygen for 5 to 40 minutes were analyzed by STM, and analyze the electrical changes in different states by STS function. We observed that the dark spot and light spot defects on the NbS2 surface tend biger with the increase of oxygen exposure time. As for the resistance near the Fermi level, it will increase with the contact with the gas, and the positive and negative bias will return such as the state before mechanical exfoliation.

並列關鍵字

STM ； STS ； NbS2 ； mechanical exfoliation ； exposed oxygen

參考文獻

[1] K. S. Novoselov,A. K. Geim,S. V. Morozov,D. Jiang,Y. Zhang, S. V. Dubonos, I. V. Grigorieva, A. A. Firsov, “Electric Field Effect in Atomically Thin Carbon Films”, Science.306(5696):666-669 (2004)

[2] Ruben Mas-Balleste Cristina Gomez-Navarro Julio Gomez-Herrero, Felix Zamora, “2D materials: to graphene and beyond”, Nanoscale.3(1):20-30 (2011)

[3] Shaoliang Yu, Xiaoqin Wu, Yipei Wang, Xin Guo, and Limin Tong, “2D Materials for Optical Modulation: Challenges and Opportunities”, Advanced Materials.29(14) (2017)

[4] K. S. Novoselov, A. Mishchenko,A. Carvalho, A. H. Castro Neto, “2D materials and van der Waals heterostructures”, Science.353(6298):6197-6206 (2016)

[5] Damien Voiry, Jieun Yang, Manish Chhowalla, “Recent Strategies for Improving the Catalytic Activity of 2D TMD Nanosheets Toward the Hydrogen Evolution Reaction”, Advanced Materials.28(29):6197-6206 (2016)