奈米鑽石/奈米金膜之室溫高效率單光子光源

Nanodiamond/nano-gold film for room temperature high-efficiency single photon sources

蔡承晏(Cheng-Yen Tsai)

指導教授 ： 張文豪

國立交通大學/理學院/電子物理系所/碩士(2013年)

https://doi.org/10.6842/NCTU.2013.00341

摘要

本論文研究室溫下具有單光子發光特性的奈米鑽石，經由與奈米金膜所產生之表面電漿耦合增快自發輻射，藉此提高單光子效率。本研究將奈米鑽石透過一層5 nm 介電材料與奈米金膜結合，經由螢光光譜和光子相干量測證實，單光子源可藉由這種混和型結構提高其單光輻射效率。透過理論模擬可證實 (N-V)─ 螢光與金屬表面電漿的耦合，因介電層的存再而使電漿子的電場因被侷限而增強，進而提升 (N-V)─ 中心的自發輻射速率。

關鍵字

奈米鑽石 ； 單光子源 ； 表面電漿

並列摘要

The thesis is devoted to develop nanodiamonds which possess single photon emission at room temperature. In order to improve the generation rate of a single photon source, nanodiamonds placed on the gold film which is coated with a dielectric material enhanced spontaneous emission could be reached. Via fluorescence spectroscopy and second-order correlation functions measurements, the single-photon sources could obtain higher emission rate by using this hybrid-system. Theory and simulation results confirmed that plasmon polariton in dielectric layer produce high-density confinement of the electric field. Hence, (N-V)- center with strong electric field can lead to a higher rate of spontaneous emission.

並列關鍵字

Nanodiamond ； Single Photon Sources ； Surface Plasmon

參考文獻

[ 2 ]N. M. Park, T. S. Kim, S. J. Park, Appl. Phys. Lett. 78, 2575, 2001

[ 8 ]M. A. Kastner, Rev. Mod. Phys. 64, 849, 1992

[ 9 ]W. H. Chang, W. Y. Chen, H. S. Chang, T. P. Hsieh, J. I. Chyi, T. M. Hsu, Phys. Rev. Lett. 96,117401, 2006

[ 10 ]A. N. Michael, Quantum Computation and Quantum Information, Cambridge, 2000

[ 12 ]Y. J. Lu, J. Kim, H. Y. Chen, C. Wu, N. Dabidian, C. E. Sanders, C. Y. Wang, M. Y. Lu, B. H. Li, X. Qiu, W. H. Chang, L. J. Chen, G. Shvets, C. K. Shih, Shangjr Gwo, Science 337, 6093, 450-453, 2012