全球環保已是眾所皆知的重要議題，世界各地都打著綠化地球的概念來保護地球，但民生用品的需求及要求的增加，使得各種製造業的興起，製造業隨之蓬勃發展，而造成水污染及空氣污染的產生。為了改善人們的生活品質，已有許多研究學者專注於光觸媒以及光催化之特性研究及開發，以此提高光觸媒催化效率，降解染整工業所排放出的染料廢水。
本研究以三嵌段兩性共聚物作為界面活性劑，Ce(NO3)3‧6H2O作為主體的前驅物，MnCl2‧4H2O為摻雜之前驅物，利用溶膠-凝膠法合成出二氧化鈰摻雜不同比例錳的試片，再分別以550 ℃、600 ℃與650 ℃進行煆燒，利用所製備之粉體進行光催化降解亞甲基藍以達到改善環境污染的目的，並藉由TGA、FTIR、XRD、SEM及TEM分析試片的微結構，並利用太陽光進行光催化，測定二氧化鈰摻雜錳的吸收率及降解效率。
根據實驗結果得知600 ℃之CM10試片的晶粒最小為17.52 nm，而其降解效率為28.39 %；降解效率最好的為650 ℃之Pure CeO2試片，降解效率為46.44 %；因此摻雜Mn能有效抑制晶粒成長，卻不能在太陽光的波段下提高降解效率，但能有與Pure CeO2接近之降解效率，如600 ℃之CM01試片，其降解效率達到44.55 %。

Global environmental protection is a well-known and important issue. The concept of greening the earth is used to protect the earth all over the world. However, the quality and demand for people's livelihood supplies have increased, which has led to the rise of various manufacturing industries, and the manufacturing industry has flourished. They cause water pollution and air pollution. In order to improve people's quality of life, many research scholars have focused on the research and development of photocatalyst and photocatalysis, in order to improve the catalytic efficiency of photocatalyst and degrade the dye wastewater which discharged from the dyeing and finishing industry.
In this study, triblock copolymer was utilized as surfactant, Ce(NO3)3‧6H2O as precursor of the host, and MnCl2‧4H2O as precursor of doping. And then, Mn-doped cerium oxide was synthesized by sol-gel method as specimen. The calcination was carried out at 550, 600 and 650 ℃, respectively. The prepared powder was then used for photocatalytic degradation of methylene blue to improve environmental pollution. The characteristic of the specimen was analyzed by TGA, FTIR, XRD, SEM and TEM. Uv-visible light was used for photocatalysis degradation, determining the absorption rate and degradation efficiency of cerium oxide doped manganese.
According to the experimental results, the minimum grain size of the CM10 at 600 ℃ is 17.52 nm, and the degradation efficiency is 28.39%. The best degradation efficiency is Pure CeO2 at 650 ℃, the degradation efficiency is 46.44%; therefore, doping Mn can effectively inhibit grain growth, but can’t improve the degradation efficiency in the visible light band, but can have degradation efficiency close to Pure CeO2, such as CM01 at 600 ℃, its degradation efficiency reaches 44.55 %

[1]. 林志忠，2016，以溶膠-凝膠法製備摻雜鈦介孔二氧化鈰及其特性研究，碩士論文，國立東科技大學，機械工程系，屏東
[2]. 蔡德純，2010，水汙染指標，取自於：http://blog.xuite.net/tct20130417/twblog/127998245-水汙染指標，造訪日期：2018年4月13日。
[3]. 莊順興，2015，「水質指標說明與應用」，朝陽科技大學，環境工程與管理系，台中。
[4]. 葉名倉，2009，「化學需氧量」，國立台灣師範大學，化學系，台北。
[5]. 康世芳，2014，經濟部工業局污染防治技術與法規宣導，淡江大學，水資源及環境工程系，台北。
[6]. 崔岱宗，2012，偶氮染料脫色細菌的脫色特性及偶氮還原機理的研究，東北林業大學，中國大陸。
[7]. 黃耀輝，「光觸媒降解水污染物應用」，國立成功大學，化工系，台南。
[8]. 晟格科技，光譜圖，晟格科技股份有限公司Chernger Tech Co，取自於：http://www.chernger.com，造訪日期：2018年3月27日。
[9]. 游勝閔、邱國創，2017，「可見光觸媒材料之技術發展」，工業技術研究院，材料與化學研究所。
[10]. 黃教程，2015，「光觸媒於環境污染物降解的應用」，國立台灣大學，環境工程學研究所，台北。
[11]. 陳永昇，2007，氧化鋅與二氧化鈰奈米結構製備及特性研究，碩士論文，國立台北科技大學，材料科學與工程研究所，台北。
[12]. 吳鴻鈞、鄒智揮，2016，「奈米儲氧材料安全性研究」，勞動部勞動及職業安全衛生研究所，台北。
[13]. 何永鈞，2014，水熱法合成二氧化錳奈米線和二氧化鈦/二氧化錳核/殼結構奈米線及其超級電容之應用，碩士論文，國立中興大學，材料科學與工程學研究所，台中。
[14]. 劉家維，2009，以溶膠-凝膠法製備奈米氧化錳，碩士論文，國立屏東科技大學，機械工程系，屏東。
[15]. 陳冠安，2016，以溶膠-凝膠法合成Mn摻雜介孔SnO2及其性質研究，碩士論文，國立屏東科技大學，機械工程系，屏東。
[16]. 趙承琛博士編著，1999，界面科學基礎，復文書局，台南。
[17]. 許明偉，2014，「物質安全資料表」，景明化工股份有限公司，苗栗。
[18]. 馬遠榮，2004，「低維奈米材料」，東華大學，應用物理研究所暨物理學系，花蓮。
[19]. 鍾啟東，2002，「奈米科技簡介」，台肥月刊，第43卷，第9期。
[20]. 賴炤銘、李錫隆，2003，「奈米材料的特殊效應與應用」，中國化學會，第61卷，第4期，第585-597頁。
[21]. 張哲瑋，2010，光催化法製備金奈米粒子的研究，碩士論文，私立東海大學，化學研究所，台中。
[22]. 廖秋峰，2009，「量子點LED簡介」，材料世界網，第276期。
[23]. 唐玄樂、史力田、賈莉、董宏偉、劉家仁，2007，「光觸媒降除空氣污染物效果評價」，中國公共衛生，第23卷，第10期，第1190-1191頁。
[24]. 曹恒光，2001，「淺談微乳液」，物理雙月刊，第23卷，第4期，第488-493頁。
[25]. Drew Myers，2004，表面、界面和膠體-原理及應用，吳大誠、朱譜新、王羅新、高緒珊譯，化學工業出版社，北京，第1-314頁。
[26]. GERARD Thomas, 2016, Chapter 1: Biochemistry – Introduction and lipids, Borzuya University, Portugal.
[27]. 刈米孝夫，1996，界面活性劑的原理與應用，第五版，王鳳編譯，高立圖書有限公司，台北，第24-34頁。
[28]. Hm, 2016, “Types of surfactants in your shampoo,” Hair Momentum, Available at: http://hairmomentum.com, Accessed 1 May 2018.
[29]. http://www.360doc.com/content/15/0422/10/17616815_465137107.shtml, Accessed 10 May 2018.
[30]. 趙承琛，1993，界面活性劑化學，復文書局，台南，第7-15頁。
[31]. C. O. Rangel-Yagui, A. Pessoa-Jr, D. Blankschtein, 2004, “Two-phase aqueous micellar systems - an alternative method for protein purification,” Brazilian Journal of Chemical Engineering, Vol. 21, No. 4.
[32]. 張莉毓，2005，奈米介孔氧化鎢在NOX氣體感測器和光致色變之應用，博士論文，國立成功大學，材料科學及工程學系，台南。
[33]. 蔡坤成，趙玉盞，謝正悅，陳妍婷，何宗漢，2014，「不同粒徑研磨粉對製備研磨墊之性質評估」，工程科技與教育學刊，第11卷，第2期，第264-273頁。
[34]. https://baike.baidu.com/item/二氧化铈, Accessed 16 May 2018.
[35]. https://zh.wikipedia.org/wiki/二氧化铈, Accessed 16 May 2018.
[36]. 蕭偉印，2006，奈米氧化鈰構形控制對乙醇轉氫效率研究，碩士論文，國立交通大學，應用化學研究所，新竹市。
[37]. Luo, J., Zha G., Wang K., Meng F., 2013, “Research Progress of Origin of Ferromagnetic in Nanoparticle CeO2,” Advances in Condensed Matter Physics, Vol. 2, pp. 1-4.
[38]. Mahmoud, W. E., Al-Ghamdi, A. A., Al-Agel, F. A., Al-Arfaj, E., Shokr, F. S., Al-Gahtany, S. A., Alshahrie, A., Hafez, M., Bronstein, L.M., Beall, G. W., 2015, “Structure and properties of the Mn doped CeO2 thin film grown on LaAlO3 (001) via a modified sol–gel spin-coating technique,” Journal of Alloys and Compounds, Vol. 640, pp. 122-127.
[39]. Fazal Abbas, Tariq Jan, Javed Iqbal , M. Sajjad Haider Naqvi , Ishaq Ahmad, 2016, “Inhibition of Neuroblastoma cancer cells viability by ferromagnetic Mn doped CeO2 monodisperse nanoparticles mediated through reactive oxygen species,” Materials Chemistry and Physics, Vol. 173, pp. 146-151.
[40]. Borker P., Salker A. V., 2007, “Solar assisted photocatalytic degradation of Naphthol Blue Black dye using Ce1−xMnxO2,” Materials Chemistry and Physics, Vol. 103, No. 2-3, pp. 336-370.
[41]. https://baike.baidu.com/item/氧化锰, Accessed 16 May 2018.
[42]. Babua, B., Kadamb, A. N., Raoc, G. T., Leeb, S. W., Byond, C., Shima J., 2018, “Enhancement of visible-light-driven photoresponse of Mn-doped SnO2 quantum dots obtained by rapid and energy efficient synthesis,” Journal of Luminescence, Vol. 195, pp. 283-289.
[43]. Bordbar, M., Jafari, S., Yeganeh-Faal, A., Khodadadi, B., 2017, “Influence of different precursors and Mn doping concentrations on the structural, optical properties and photocatalytic activity of single-crystal manganese-doped ZnO,” Journal of the Iranian Chemical Society, Vol. 14, No. 4, pp. 897-906.
[44]. Wang, L., Wang, P., Huang, B., Ma, X., Wang, G., Dai, Y., Zhang, X., Qin, X., 2017, “Synthesis of Mn-doped ZnS microspheres with enhanced visible light photocatalytic activity,” Applied Surface Science, Vol. 391, Part B, pp. 557-564.
[45]. 黃文魁，2003，「奈米級二氧化鈦的液相製備方法探討比較」，經濟部技術處ITIS計畫，取自於：http://www.itis.org.tw，造訪日期：2018年3月29日。
[46]. http://www.mse.fcu.edu.tw/wSite/public/Attachment/f1348051531886.pdf, Accessed 16 July 2018.
[47]. 葛煥彰，2006，膠體與界面科學，國立台灣大學，工學院，台北。
[48]. TWWORD，2018，「縮聚反應」，台灣WORD，取自於：http://www.twword.com，造訪日期：2018年5月1日。
[49]. 鐘金湯，2004，「偶氮染料及其代謝產物的化學結構與毒性關係的回顧與前瞻」，環境與職業醫學，第21卷，第1期，第58-62頁。
[50]. 蔡冬鳴，任南琪，2006，「不同晶型錳氧化物去除水中亞甲基藍染色的研究」，環境科學學報，第26卷，第12期，第1971-1976頁。
[51]. ZWBK，2018，「亞甲基藍」，中文百科在線，取自於：http://www.zwbk.org，造訪日期：2018年7月15日
[52]. 林彥志，2000，TiO2光觸媒電極分解亞甲基藍之變因探討及動力學研究，碩士論文，國立台灣大學，化學工程學研究所，台北。
[53]. 洪邦彥，2003，WOx/TiO2 可見光應答光觸媒之研究，碩士論文，國立清華大學，化學工程系，新竹。
[54]. 林淑君，2012，ZnWO4 – TiO2複合式光觸媒對亞甲基藍處理之研究，碩士論文，國立屏東科技大學，環境工程與科學系，屏東。
[55]. Kumar, P., Kumar, P., Kumar, A., Meena, R.C., Tomar, R., Chand, F., Asokan, K., 2016, “Structural, morphological, electrical and dielectric properties of Mn doped CeO2,” Journal of Alloys and Compounds, Vol. 672, pp. 543-548.
[56]. 翁于婷，2015，「紅外線光譜(二)」，科學Online。
[57]. Wade, L.G., 2006, “Organic chemistry,” Pearson Education International: Upper Saddle River, pp. 531.
[58]. http://ebook-4download.com/ir-spectrum-table.html/ir-introduction-throughout-ir-spectrum-table, Accessed 16 July 2018.
[59]. 林麗娟，1994，「X光繞射原理及其應用」，工業材料，第86期，第100-109頁。
[60]. 張育唐，陳藹然，2011，「X-光繞射與布拉格定律」，科學Online。
[61]. 陳力俊等著，1989，材料電子顯微鏡學，行政院國家科學委員會精密儀器發展中心，新竹，第285-318頁。
[62]. 林智仁，羅聖全，2003，「場發射穿透式電子顯為鏡簡介」，工業材料雜誌，第201期，第90-98頁。
[63]. 環境檢驗檢量線製備及查核指引，2004，中華民國行政院環境保護署環境檢驗所。
[64]. Krongthong Kamonsuangkasem, Supaporn Therdthianwong, Apichai Therdthianwong, Nirawat,Thammajak, 2017, “Remarkable activity and stability of Ni catalyst supported on CeO2-Al2O3 via CeAlO3 perovskite towards glycerol steam reforming for hydrogen production,” Applied Catalysis B: Environmental, Vol. 218, pp. 650-663.
[65]. Yanet Piña-Pérez, Francisco Tzompantzi-Morales, Raúl Pérez-Hernández, Rubén Arroyo-Murillo, Próspero Acevedo-Peña, Ricardo Gómez-Romero, 2017, “Photocatalytic activity of Al2O3 improved by the addition of Ce3+/Ce4+ synthesized by the sol-gel method. Photodegradation of phenolic compounds using UV light,” Fuel, Vol. 198, pp. 11-21.
[66]. Ghodsi, F. E., Tepehan, F. Z., Tepehan, G. G., 2011, “Derivation of the optical constants of spin coated CeO2–TiO2–ZrO2 thin films prepared by sol–gel route,”Vol. 72, Issue 6, pp. 761-767.
[67]. Karolewicz, B., Gajda, M., Go´rniak, A., Owczarek, A., Mucha, I., 2017, “Pluronic F127 as a suitable carrier for preparing the imatinib base solid dispersions and its potential in development of a modified release dosage forms,” Journal of Thermal Analysis and Calorimetry, Vol. 130, No. 1, pp. 383-390.
[68]. Beril Melbiah, J.S., Nithya, D., Mohan, D., 2017, “Surface modification of polyacrylonitrile ultrafiltration membranes using amphiphilic Pluronic F127/CaCO3 nanoparticles for oil/water emulsion separation,” Colloids and Surfaces A-Physicochemical and Engineering Aspects, Vol. 516, pp. 147-160.
[69]. K. Mani Rahulan, N. Angeline Little Flower, R. Annie Sujatha, P. Mohana Priya, C. Gopalakrishnan, 2018, “Third order nonlinear optical properties of Mn doped CeO2 nanostructures,” Optics & Laser Technology, Vol. 101, pp. 358-362.
[70]. Meng, L., Wang, J., Sun, Z., Zhu, J., Li, H., Wang, J., Shen, M., 2018, “Active manganese oxide on MnOx–CeO2 catalysts for low-temperature NO oxidation: Characterization and kinetics study,” Journal of Rare Earths, Vol. 36, No. 2, pp. 142-147.
[71]. Lin, X., Li, S., He, H., Wu, Z., Wu, J., Chen, L., Ye, D. Fu, M., 2018, “Evolution of oxygen vacancies in MnOx-CeO2 mixed oxides for soot oxidation,” Applied Catalysis B: Environmental, Vol. 223, pp. 91-102.
[72]. 高清芬，2005，光柵位移干涉術，博士論文，國立交通大學，光電工程研究所，新竹。
[73]. Edington, J. W., 1985, The Operation and Calibration of The Electron Microscope, Erudition Publications, New York.
[74]. 李宗修，2017，以溶膠-凝膠法製備釔、鈰共摻雜氧化鋅及其特性研究，碩士論文，國立屏東科技大學，機械工程系，屏東。
[75]. 呂道元，2015，以溶膠-凝膠法製備介孔二氧化鈰摻雜鋯及其特性研究，碩士論文，國立屏東科技大學，機械工程系，屏東。