The use of additive manufacturing (AM) is expanding rapidly. However, the mechanical behavior of printing materials has yet to be fully elucidated. In this study, we examined UV-cured photopolymers designed for use in PolyJet systems. We tested the impact strength and wear characteristics of the photopolymer in accordance with ASTM D256-10 and ASTM D4060-10, respectively. When the impact test piece was placed in the transverse direction, it had the best impact strength. Its impact strength was 27.25 J/m. When the wear test piece was placed at an angle of 45 degrees, the wear weight loss was 0.0268 g. It had good wear characteristics.