Friction and Wear Comparison Tests on Different Surface Coatings and Shapes
並列摘要
This study describes an experimental comparison of the tribological behavior of three coatings for advanced applications. In particular, couplings of steel with coatings in cast and electroplated bronze, and in WC/C were tested by means of a reciprocating apparatus and a pin-on-disc test rig. Different sliding velocities were applied and the dynamic coefficient of friction estimated. Additionally, comparative evaluations of the wear behavior were carried out. The results pointed out a better performance of the WC-C coating compared to the others, showing both a lower coefficient of friction and lower wear, under almost all tested conditions.
被引用紀錄
Chen, H. C. (2008). 應用於虛擬實境的即時雙向耦合船舶模擬 [master's thesis, National Taiwan University]. Airiti Library. https://doi.org/10.6342/NTU.2008.02276
延伸閱讀
- Jadayil, W. M. A. (2015). Surface and Subsurface Defects Investigation of Ni-Ti Samples Processed by Different Fabrication Methods. Research Journal of Applied Sciences, Engineering and Technology, 11(11), 1190-1195. https://www.airitilibrary.com/Article/Detail?DocID=20407467-201512-201601200035-201601200035-1190-1195
- 劉濬帆（2014）。Vision Image Inspections of Surface Roughness and Byproduct Color for Cutting Parts〔碩士論文，國立虎尾科技大學〕。華藝線上圖書館。https://doi.org/10.6827/NFU.2014.00022
- Spivak, Y. M., Mjakin, S. V., Moshnikov, V. A., Panov, M. F., Belorus, A. O., & Bobkov, A. A. (2016). Surface Functionality Features of Porous Silicon Prepared and Treated in Different Conditions. Journal of Nanomaterials, 2016(), 505-512-053. https://doi.org/10.1155/2016/2629582
- Adoberg, E., Podgurski, V., Peetsalu, P., Lind, L., Mikli, V., Hvizdos, P., & Kulu, P. (2012). The Effect of Surface Pre-Treatment and Coating Post-Treatment to the Properties of TiN Coatings. Estonian Journal of Engineering, 18(3), 185-192. https://www.airitilibrary.com/Article/Detail?DocID=17367522-201209-201311120035-201311120035-185-192
- 陳德發、李俊毅、賴嘉均、賴嘉宏、陳狄成（2016）。The effect of sheet metals to different process condition。鍛造，25(4)，25-29。https://www.airitilibrary.com/Article/Detail?DocID=1023750x-201612-201902130031-201902130031-25-29