Title

SUS441表面鍍覆錳鈷氧化物保護膜之微結構及電化學特性

Translated Titles

A Study on the Microstructural and Electrochemical Properties of SUS441 Manganese Cobalt Oxide Coating Films

Authors

曾惠萍(H.P. Tseng);雍敦元(T.Y. Yung);楊朋(Peng Yang);劉建國(C.K. Liu);李瑞益(R.Y. Lee)

Key Words

脈衝直流磁控濺鍍 ; 錳鈷氧化物 ; 電化學阻抗頻譜 ; 等效電路模擬 ; 高溫面積比電阻 ; Pulsed DC magnetron sputtering ; Manganese-cobalt oxide ; Electrochemical Impedance Spectrum ; Equivalent circuit model ; Area Specific Resistance

PublicationName

鑛冶:中國鑛冶工程學會會刊

Volume or Term/Year and Month of Publication

61卷3期(2017 / 09 / 01)

Page #

96 - 102

Content Language

繁體中文

Chinese Abstract

本研究於商用之肥粒鐵系SUS441 不銹鋼基板表面,以脈衝直流磁控濺鍍方式分別鍍覆1.5 μm 及3.5 μm 之錳鈷氧化物(Mn, Co)_3O_4(MCO) 保護膜, 經800 ℃,1800 小時2 LPM空氣下熱處理後,探討其保護膜層及基板氧化層組成、微結構與電化學阻抗之關係,並比較不同預氧化條件(800℃,25 小時及850℃,25 小時)處理後,鍍覆3.5 μm 之MCO 保護層對電性之影響。試樣經800℃熱處理1800 小時後,量測室溫下之電化學阻抗頻譜(EIS) 及高溫面積比電阻(ASR),建立等效電路模型模擬各膜層之阻抗並與XRD、SEM/EDS 之分析觀察比較,透過數值模擬了解各氧化層間之電性關係,並提出反應機制。研究結果顯示,鍍覆MCO 能有效抑制鉻元素擴散,提高導電效率,經800℃空氣下1800 小時之熱處理,MCO 與基板氧化層形成一穩定且擁有較佳電性之(Mn, Co, Cr)_3O_4 層,且於MCO 鍍膜厚度為3.5 μm 之試樣,擁有最佳之電性。

English Abstract

We investigated the microstructural and electrochemical properties of (Mn, Co)_3O_4 (MCO) protective films coated on SUS441. SUS441 were pre-oxidized in an ambient atmosphere at 800°C and 850°C for 25 hours, respectively. The thickness of MCO films were 1.5 and 3.5 μm then deposited on the surface of SUS441 by using pulsed DC magnetron sputtering technique. The as-coated specimens aged at 800°C for 1800 hours in an air atmosphere with a flow rate of 2 LPM. After aging, the crystalline phases, microstructures, and electrochemical resistances of MCO coated SUS441 were examined by using XRD, SEM/EDS, electrochemical impedance spectroscopy (EIS), and Area Specific Resistance (ASR). A proper equivalent circuit model was used to interpret the results of EIS. The pre-oxidized specimen of SUS441 with a 3.5 μm MCO coating had the best electrochemical Properties.

Topic Category 工程學 > 礦冶與冶金工程
Times Cited
  1. 黃喆恩(2015)。鐵離子及pH影響通氣的零價鋁系統氧化移除水溶液中之三價砷。中興大學土壤環境科學系所學位論文。2015。1-95。 
  2. 陳嘉弘(2006)。單體非重複之寡聯芳香環與四取代呋喃化合物。臺灣大學化學研究所學位論文。2006。1-113。 
  3. 洪文誼(2005)。非晶態有機半導體及有機發光材料中載子傳輸特性之研究。臺灣大學光電工程學研究所學位論文。2005。1-188。